Abstract:Surface modification and deuterium (D) retention in pure tungsten (W) and tungsten-rhenium (W-Re) alloys with Re concentration of 1, 3, 5 and 10 wt.% were investigated after exposure to D plasma with an incident energy of 38 eV/D at about 400 K and various fluences ranging from 7.2 × 1023 to 2.6 × 1025 D/m2. It is found that blistering depends strongly on the exposure fluence for both W and W-Re alloy samples. When the D fluence is higher than 2.8 × 1024 D/m2, the surface of W is covered by two types of blisters. One type is small blisters (<2 μm), which appeared in groups only on grains with surface orientation close to (111). The other type is large-sized (>8 μm) and extents over several grains. In the cases of W-Re alloys, only small blisters can be observed on their surface. The blisters on the surface of W-Re alloys preferentially appeared on grains with surface orientation close to (111). Cross-section views of blisters show that the blisters on W-Re alloys always originate from intra-granular cavities. The small and large blisters on W originate from intra- and inter-granular cavities, respectively. The surface blistering fluence threshold for W-Re alloys is lower than for W. For both types of materials, rupture of blisters occurs if the underlying crack reaches the surface at the edge of a blister. The number of ruptured blisters increases with increasing D fluence. TDS results show that there is an additional high-temperature peak at ∼ 800 K in W-Re alloys. The amount of D released from W and W-Re alloys increases with increasing D fluence. In addition, the accumulation of D in W-Re alloys is not noticeably influenced by the amount of Re doping at the exposure temperature of ∼ 400 K.

Effect of Anisotropic Grain Boundaries on the Surface Blistering of Tungsten Induced by Deuterium Plasma Exposure

Deuterium Blistering in Tungsten and Tungsten Vanadium Alloys

Blistering Behavior and Deuterium Retention in Tungsten Vanadium Alloys Exposed to Deuterium Plasma in the Linear Plasma Device STEP

Effects of Tantalum Alloying on Surface Morphology and Deuterium Retention in Tungsten Exposed to Deuterium Plasma

Effect of Exposure Temperature on Deuterium Retention and Surface Blistering of Tungsten Exposed to Sequential Nitrogen and Deuterium Plasma

Suppression of Deuterium-Induced Blistering in Pre-Damaged Tungsten Exposed to Short-Duration Deuterium Plasma

Surface modification and deuterium retention in hot-rolled potassium doped tungsten alloy exposed to deuterium plasma

Surface modification and deuterium retention of tungsten and tungsten-rhenium alloys exposed to deuterium plasma

Effect of thickness on the blistering of tungsten exposed to deuterium plasma

Lateral Stress Induced Blistering of Tungsten Exposed to Deuterium Plasma

Influence of Nitrogen Pre-Irradiation at Different Temperatures on Surface Blistering and Deuterium Retention in Tungsten

Decreased Surface Blistering and Deuterium Retention in Potassium-Doped Tungsten Exposed to Deuterium Plasma Following Ion Irradiation

Aggravated Blistering and Increased Deuterium Retention in Iron-Damaged Tungsten after Exposure to Deuterium Plasma with Various Surface Temperatures

Decreased surface blistering and deuterium retention in potassium potassium-doped tungsten exposed to deuterium plasma following ion irradiation

Surface Modification and Deuterium Retention of High Energy Rate Forging W-Y2O3exposed to Deuterium Plasma

Deuterium Distribution and Behavior of Blisters in Pre-Damaged and Undamaged Tungsten

Surface blistering and deuterium retention behaviors in pure and ZrC-doped tungsten exposed to deuterium plasma

Surface Modification and Deuterium Retention in Rhenium Doped Tungsten Exposed to Low Energy Deuterium Plasma

Deuterium Retention and Surface Blistering in Non-Damaged and Damaged Tungsten after Repetitive Plasma Exposure and Outgassing

Surface Blistering and D Desorption in High-Energy-rate Forging W, W-Y2O3, W-TiC Exposed to Deuterium Plasma

Dependence of blistering and deuterium retention on damage depth in damaged tungsten exposed to deuterium plasma