Abstract:A wire arc additive manufacturing system, based on cold metal transfer technology, was utilized to manufacture the Al-Mg alloy walls. ER5556 wire was used as the filler metal to deposit Al-Mg alloys layer by layer. Based on the orthogonal experiments, the process parameters of the welding current, welding speed and gas flow, as well as interlayer residence time, were adjusted to investigate the microstructure, phase composition and crystal orientation as well as material properties of Al-Mg alloyed additive. The results show that the grain size of Al-Mg alloyed additive becomes smaller with the decrease of welding current or increased welding speed. It is easier to obtain the additive parts with better grain uniformity with the increase of gas flow or interlayer residence time. The phase composition of Al-Mg alloyed additive consists of α-Al matrix and γ (Al12Mg17) phase. The eutectic reaction occurs during the additive manufacturing process, and the liquefying film is formed on the α-Al matrix and coated on the γ phase surface. The crystal grows preferentially along the <111> and <101> orientations. When the welding current is 90 A, the welding speed is 700 mm/min, the gas flow is 22.5 L/min and the interlayer residence time is 5 min, the Al-Mg alloy additive obtains the highest tensile strength. Under the optimal process parameters, the average grain size of Al-Mg alloyed additive is 25 μm, the transverse tensile strength reaches 382 MPa, the impact absorption energy is 26 J, and the corrosion current density is 3.485 × 10−6 A·cm−2. Both tensile and impact fracture modes of Al-Mg alloyed additive are ductile fractures. From the current view, the Al-Mg alloys manufactured by WAAM-CMT have a better performance than those produced by the traditional casting process.

Forming Characteristics and Mechanism of Variable Polarity TIG-based Wire Arc Additive Manufacturing of Al–Mg-Zn-Cu Alloy

Impact of Process Parameters on Forming Quality and Deposition Efficiency of Unsupported Rods in Wire Arc Additive Manufacturing

Multi-physical modelling of alloy element transportation in wire arc additive manufacturing of a γ -TiAl alloy

Comparative Study of Solidification Behaviors of Weld Pool Through Modelling of Heat Transfer and Fluid Flow During Single- and Multiplelayer Deposits of 2319-Aluminum Alloy Based on Variable Polarity Gas Tungsten Arc Welding

Microstructure characteristics under varying solidification parameters in different zones during CMT arc additive manufacturing process of 2319 aluminum alloy

Effects of Deposition Paramaters on the Microstructure Evolution of Wire Arc Additive Manufactured Al–Zn–Mg–Cu Alloy

Metal transfer and forming behavior of bypass-coupled variable polarity plasma arc additive manufacturing

Numerical Simulation of Arc Characteristics and Multi-Layer Deposition of Cu Alloys Fabricated by Wire Arc Additive Manufacturing

Microstructures and Properties of Al-Mg Alloys Manufactured by WAAM-CMT

Multi-layer Deposition Mechanism in Ultra High-Frequency Pulsed Wire Arc Additive Manufacturing (WAAM) of NiTi Shape Memory Alloys

Wire arc additive manufacturing of Al-Zn-Mg-Cu alloy: Microstructures and mechanical properties

Forming characteristic analysis in twin tungsten electrode – wire electrode indirect arc based additive manufacturing

Width Prediction of Aluminium Alloy Weld Additively Manufactured by TIG Arc

Multiscale modelling of microstructure, micro-segregation, and local mechanical properties of Al-Cu alloys in wire and arc additive manufacturing

Microstructures and Mechanical Properties of Wire Arc Additive Manufactured 5183-Al: Influences of Deposition Dimensions

Manipulating molten pool in in-situ additive manufacturing of Ti-22Al-25Nb through alternating dual-electron beams

Metal Transfer Behavior and Molten Pool Dynamics in Cold Metal Transfer Pulse Advanced Additive Manufacturing of 7075 Aluminum Alloy

Manipulating Molten Pool in In-Situ Additive Manufacturing of Ti-22Al-25 Nb Through Alternating Dual-Electron Beams

Microstructures and Mechanical Properties of Al–Zn–Mg Aluminium Alloy Samples Produced by Wire + Arc Additive Manufacturing

High-efficient hybrid arc and friction stir additive manufacturing of high-performance Al-Cu-Mg-Ag-Zr alloy: Microstructural evolution and precipitation behaviors with Ω/L1 2 co-precipitates

Short Circuiting Transfer, Formation, and Microstructure of Ti-6Al-4V Alloy by External Longitudinal Magnetic Field Hybrid Metal Inert Gas Welding Additive Manufacturing