Abstract:Ceramic-reinforced aluminum-based composites are ideal materials for lightweight structural parts. However, as the content of the ceramic reinforcement phase increases, the toughness of the composites will decrease, resulting in a decrease in the safety of the composites during service. Therefore, how to achieve the matching of high strength and toughness of composite materials is a problem that has always existed in the preparation of ceramic reinforced aluminum matrix composites. According to the idea of bionics, the nacre-inspired TiB2/Al-Cu composites with different ceramic initial solid content (20vol.%, 30vol.%, 40vol.%) were successfully prepared by freezing casting and pressure infiltration. The microstructures and mechanical properties of nacre-inspired TiB2/Al-Cu composites were studied by optical microscopy (OM), scanning electron microscopy (SEM), X-ray diffraction (XRD) and mechanical testing. The experimental results show that with the increase of the initial solid content of the ceramic, the thickness of the ceramic sheet in the composite material increases, while the thickness of the metal sheet layer decreases. The compressive strength of the composite material is improved, but the bending strength and fracture toughness decrease. The nacre-inspired TiB2/Al-Cu composites with 20vol.% ceramic initial solid content has the better fracture toughness, reaching 20.59±1.5 MPa·m1/2; The nacre-inspired TiB2/Al-Cu composites with 40vol.% ceramic initial solid content has the better compressive strength, reaching 670±20 MPa. This is mainly because as the initial solid content of the ceramic in the composite material increases, the nacre-inspired composite material are more prone to interface delamination, the toughening effect of the layered composite material through alloy plastic deformation is weakened; at the same time, the toughening effect of crack deflection, interface peeling, and crack branching is reduced.

Development of a Nacre-Like Metal-Ceramic Composite with a Brick-and-mortar Structure and High Ceramic Content

Bioinspired Hydroxyapatite/Poly(methyl Methacrylate) Composite with a Nacre‐Mimetic Architecture by a Bidirectional Freezing Method

Conch‐Shell‐Inspired Tough Ceramic

Cost-effective Fabrication of Bio-Inspired Nacre-Like Composite Materials with High Strength and Toughness

Fabrication and Characterisation of Alumina/aluminium Composite Materials with a Nacre-Like Micro-Layered Architecture

Microstructures and Mechanical Characterizations of High-Performance Nacre-Inspired Al/Al2O3 Composites

Nacre-mimetic Composite with Intrinsic Self-Healing and Shape-Programming Capability

Construction of nacre-mimetic composites with a “brick-and-mortar” architecture based on structural defects in ice-templating

Effects of Ceramic Lamellae Compactness and Interfacial Reaction on the Mechanical Properties of Nacre-Inspired Al/Al2O3–ZrO2 Composites

Fabrication and Characterization of Nacre-Inspired Metal/ceramic Composites Containing AlN Nanowhiskers

Microstructure and Mechanical Properties of Nacre-Inspired TiB2/Al-Cu Composites

Nacre-like carbon fiber-reinforced biomimetic ceramic composites: Fabrication, microstructure, and mechanical performance

Bioinspired ceramic-polymer composites with hierarchical nacre-mimetic structure via accumulative rolling technique

A Novel Approach to the Fabrication of Lamellar Al2O3/6061Al Composites with High-Volume Fractions of Hard Phases

Developing High-Performance Laminated Cu/TiC Composites Through Melt Infiltration of Ni-doped Freeze-Cast Preforms

A Strong, Tough, and Stable Composite with Nacre-Inspired Sandwich Structure

Artificial Nacre with High Toughness Amplification Factor: Residual Stress‐Engineering Sparks Enhanced Extrinsic Toughening Mechanisms

Bioinspired Nacre-Like Alumina with a Metallic Nickel Compliant Phase Fabricated by Spark-Plasma Sintering

Achieving High Strength and Toughness by Engineering 3D Artificial Nacre-Like Structures Inti6al4v-Ti Metallic Composite

Strong and Tough Magnesium-Max Phase Composites with Nacre-Like Lamellar and Brick-and-mortar Architectures

Synthesis of damage-tolerant Cu-matrix composites with nacre-inspired laminate-reticular hierarchical architecture via tuning compositional wettability