Abstract:Biodegradable Zn alloys show great potential for vascular stents due to their moderate degradation rates and acceptable biocompatibility. However, the poor mechanical properties limit their applications. In this study, low alloyed Zn-2Cu-xLi (x = 0.004, 0.01, 0.07 wt %) alloys with favorable mechanical properties were developed. The microstructure consists of fine equiaxed η-Zn grains, micron, submicron-sized and coherent nano ε-CuZn4 phases. The introduced Li exists as a solute in the η-Zn matrix and ε-CuZn4 phase, and results in the increase of ε-CuZn4 volume fraction, the refinement of grains and more uniform distribution of grain sizes. As Li content increases, the strength of alloys is dramatically improved by grain boundary strengthening, precipitate strengthening of ε-CuZn4 and solid solution strengthening of Li. Zn-2Cu-0.07Li alloy has the optimal mechanical properties with a tensile yield strength of 321.8 MPa, ultimate tensile strength of 362.3 MPa and fracture elongation of 28.0 %, exceeding the benchmark of stents. It also has favorable mechanical property stability, weak tension compression yield asymmetry and strain rate sensitivity. It exhibits uniform degradation and a little improved degradation rate of 89.5 μm∙year-1, due to the improved electrochemical activity by increased ε-CuZn4 volume fraction, and generates Li2CO3 and LiOH. It shows favorable cytocompatibility without adverse influence on endothelial cell viability by trace Li+. The fabricated microtubes show favorable mechanical properties, and stents exhibit an average radial strength of 118 kPa. The present study indicates that Zn-2Cu-0.07Li alloy is a potential and promising candidate for vascular stent applications. STATEMENT OF SIGNIFICANCE: Zn alloys are promising candidates for biodegradable vascular stents. However, improving their mechanical properties is challenging. Combining the advantages of Cu and trace Li, Zn-2Cu-xLi (x < 0.1 wt %) alloys were developed for stents. As Li increases, the strength of alloys is dramatically improved by refined grains, increased volume fraction of ε-CuZn4 and solid solution of Li. Zn-2Cu-0.07Li alloy exhibits a TYS exceeding 320 MPa, UTS exceeding 360 MPa and fracture EL of nearly 30 %. It shows favorable mechanical stability, degradation behaviors and cytocompatibility. The alloy was fabricated into microtubes and stents for mechanical property tests to verify application feasibility for the first time. This indicates that Zn-2Cu-0.07Li alloy has great potential for vascular stent applications.

Study on Properties of Zn-xMg (x = 0.5, 0.8, 1) Alloys for Potential Stent Material

Effect of Zn Concentration on the Microstructure and Mechanical Properties of Al-Mg-Si-Zn Alloys Processed by Gravity Die Casting

The Microstructure and Mechanical Properties of As-cast Mg-10Gd-3Y-xZn-0.6Zr (x=0, 0.5, 1 and 2 Wt%) Alloys

Microstructures and Properties of Biomedical Mg-Zn-Sn-Zr Rolled Alloys

The Properties Evolution of Medical Mg–Zn Alloys Prepared by Semi-solid Powder Moulding

Microstructures and Mechanical Properties of Hot-extruded Mg-6Zn-xCu-0.6Zr(x=0,0.5,1.0,1.5) Alloys

Evaluation of As‐extruded Ternary Zn–Mg–Zr Alloys for Biomedical Implantation Material: in Vitro and in Vivo Behavior

Synthesis and Properties of Mg-Mn-Zn Alloys for Medical Applications

Microstructure, Mechanical, and Corrosion Properties of Extruded Low-Alloyed Mg-xZn-0.2Ca Alloys

The microstructure and properties of cyclic extrusion compression treated Mg-Zn-Y-Nd alloy for vascular stent application

Effect of Hot Extrusion on the Microstructure, Mechanical Properties, and Corrosion Behavior of Mg–11Li–3Al–2Zn–1.5Nd–0.2Zr Alloy

Systematical evolution on a Zn–Mg alloy potentially developed for biodegradable cardiovascular stents

Microstructures and mechanical properties of as-extruded Mg–5Sn–1Zn–xAl (x=1, 3 and 5) alloys

Effect of Zn Content on the Microstructure and Mechanical Properties of Mg–Al–Sn–Mn Alloys

Effect of Al on the Microstructure and Mechanical Properties of Mg–6Zn–2Sn–0.5Mn Alloy

Developing Zn-2Cu-xLi (x < 0.1 wt %) alloys with suitable mechanical properties, degradation behaviors and cytocompatibility for vascular stents

Microstructure, Mechanical Properties, Corrosion Behavior and Biocompatibility of As-Extruded Biodegradable Mg–3Sn–1Zn–0.5Mn Alloy

Microstructure, Mechanical Properties and Corrosion Behavior of Mg-Zn-Zr Alloys with Different Compositions

Microstructures, Mechanical Properties and in Vitro Corrosion Behavior of Biodegradable Zn Alloys Microalloyed with Al, Mn, Cu, Ag and Li Elements

Biodegradable Zn-Cu-Mn alloy with suitable mechanical performance and in vitro degradation behavior as a promising candidate for vascular stents

Effect of Al Addition on Microstructure, Mechanical, and Corrosion Properties of Hot Extruded Mg-2.0Zn-0.4Mn Alloy