Enabling a compatible Li/garnet interface via a multifunctional additive of sulfur

Jie Wang,Saisai Zhang,Shaokang Song,Jintao Liu,Zhaolin Li,Hailei Zhao
DOI: https://doi.org/10.1039/d2ta05912f
IF: 11.9
2022-01-01
Journal of Materials Chemistry A
Abstract:Ceramic-based solid-state batteries with lithium metal anode show great potential to realize a battery revolution because of their features of nonflammability and high energy density. Among the inorganic electrolytes, garnet-type Li7La3Zr2O12 attracts much attention as a promising alternative owing to its advantages of high ionic conductivity, wide electrochemical voltage window, and excellent thermal stability. However, the critical issue of the insufficient lithium-electrolyte interface contact significantly hinders its practical application. Herein, an intimate physical connection between the Li anode and garnet is achieved by improving the wettability of molten Li with multifunctional sulfur (S) addition. The generated Li2S with high ionic conductivity could also provide an extended interface area for charge transfer, enabling a reduced local current density and thus favoring the rate performance. Because of the tightly increased contact area and the homogenized interface electric-field distribution, the fabricated symmetric cells with an optimal Li-Li2S anode (LS10: 10 wt% S addition) show a significantly decreased interfacial resistance (12.4 omega cm(2)) and a stable Li plating/stripping performance for over 900 h at 0.2 mA cm(-2). The constructed LS10|Li6.4La3Zr1.4Ta0.6O12|LiFePO4 full cell delivers a high reversible specific capacity of 154.7 mA h g(-1) at 0.1C and stable cycling with a capacity fading rate of similar to 0.033% per cycle.
What problem does this paper attempt to address?