Chemical and Mechanical Stability of an Ion-Exchanged Lithium Disilicate Glass in Artificial Saliva

X. C. Li,Z. X. Chen,D. Li,W. Z. Liu,M. Meng

DOI: https://doi.org/10.1016/j.jmbbm.2022.105563

2023-01-01

Abstract:Multi-component lithium disilicate (LD) glasses were ion-exchanged in a pure or mixed nitrate salt bath. The surface morphologies, mechanical properties, chemical stability and ion leaching of ion-exchanged LD glasses before and after storage in artificial saliva for 21 days were investigated. It can be found that chemical stability of ion-exchanged LD glass was temperature-dependent. The residual compressive stress induced by ion-exchange increased the chemical potential of alkali ions in glass, and the ion-exchanged LD glass, especially 235 °C/64 h group, chemical stability in artificial saliva for 21 days were deteriorated. Back-exchange treatment could relax the stress on the outermost layer of the ion-exchanged LD glass without deteriorating its strengthening effect, and back-exchanged LD glass presented good chemical and mechanical stability in artificial saliva. The results might help to enhance the service stability of ion-exchanged LD glass-ceramics in the oral condition.