Growth and Electrical Properties of Yb3+A-site Doped PMNT:Yb Single Crystal

Siqin Yan,Zhigang Sun,Xin Chen,Huiyu Qian,Tao Zhao,Hongbing Chen,Linwen Jiang

DOI: https://doi.org/10.1016/j.jpcs.2022.111103

IF: 4.383

2023-01-01

Journal of Physics and Chemistry of Solids

Abstract:0.01Yb2O3-0.69 Pb(Mg1/3Nb2/3)O3-0.30PbTiO3 (PMNT:Yb) single crystal with the size of o25 x 90 mm2 was successfully grown by the seed-guided Bridgman method. The electrical properties such as dielectric behavior, piezoelectric coefficient and ferroelectric properties were systematically characterized. The optimal d33 reached 2670 pC/N under the alternating current polarization conditions of 15 Hz, 14 kV/cm and 10 cycles. The crystal structure changed from the rhombohedral phase to the tetragonal phase during the growth process, and the phase transition temperature is 95 degrees C-100 degrees C, and TC is 128 degrees C-135 degrees C. Under the electric field of 20 kV/cm and frequency of 15 Hz, the coercive field EC of the crystal is 3.7 kV/cm, and the residual polarization Pr is 26.4 mu C/ cm2. Under alternating current polarization mode, the ferroelectric domain becomes periodically dense and regular, and the size of electric domain is uniform. In the wavelength range of 200-2000 nm, the absorption edge of PMNT:Yb crystal is 400 nm, and the wafer transmittance under unpolarized mode, direct current polarization mode and alternating current polarization mode are 41%-45%, 55%-58%, and 58%-63%, respectively. The PT -based relaxor ferroelectric crystals have great potential in the application of acoustic optical-electrical multi-functional couplers.