Growth and electrical properties of Pb(Sc1/2Nb1/2)O3-Pb(Mg1/3 Nb2/3)O3-PbTiO3 ternary single crystals by a modified Bridgman technique

Yiping Guo,Haiqing Xu,Haosu Luo,Guisheng Xu,Zhiwen Yin

DOI: https://doi.org/10.1016/S0022-0248(01)01362-8

IF: 1.8

2001-01-01

Journal of Crystal Growth

Abstract:Single crystals of 0.05Pb(Sc1/2Nb1/2)O3–0.63Pb(Mg1/3Nb2/3)O3–0.32PbTiO3 have been grown directly from melt by a modified Bridgman technique. The crystals with perovskite structure were 15mm in diameter and 20mm in length. The segregation during the growth of the single crystals was studied by means of X-ray diffraction analysis. The results show that PbTiO3 content increases throughout the crystal growth. The electrical properties of the single crystals oriented along the [001] axis have been characterized. The plates cut from the seed end of a boule exhibited a permittivity (ε33ε0) of about 3500, dielectric loss tangent (tgδ)<1%, dielectric constant peaks at 162°C, piezoelectric constant (d33)≈1200pC/N, and electromechanical coupling factor (kt)≈60% for the thickness mode. Our results show that xPb(Sc1/2Nb1/2)O3–yPb(Mg1/3Nb2/3)O3–(1-x-y)PbTiO3 single crystals are promising for a wide range of electromechanical transducer applications.