Enhanced Electrical Properties of Novel Pb(Ni1/3Nb2/3)O3–BiScO3–PbTiO3Ternary System Near Morphotropic Phase Boundary

Dali Wang,Zhaohua Jiang,Bin Yang,Shantao Zhang,Mingfu Zhang,Feifei Guo,Wenwu Cao

DOI: https://doi.org/10.7567/jjap.52.101101

IF: 1.5

2013-01-01

Japanese Journal of Applied Physics

Abstract:A novelxPb(Ni1/3Nb2/3)O3–(1-x)(0.30BiScO3–0.70PbTiO3) (PNN–BS–PT) ternary system was prepared by the columbite precursor method. The phase structure, microstructure, and electrical properties of ceramics of this system were investigated to identify the morphotropic phase boundary (MPB) composition of this system. The MPB with coexisting rhombohedral–tetragonal phases of PNN–BS–PT was located at approximatelyx=0.35, confirmed by their respective electric properties. With increasing PNN content, the coercive fieldEC, the Curie temperatureTC, and the rhombohedral-to-tetragonal phase transition temperatureTR–Twere found to decrease and showed nearly linear dependences on their compositions. The enhanced properties were achieved in the MPB composition withx=0.35, which are as follows: dielectric constant εr=3160 (1 kHz), piezoelectric coefficientd33=490 pC/N, and electromechanical coupling factorkp=0.44. In addition, a large bipolar strain on the order of 0.6% was achieved for the composition when an electrical fieldE=40 kV/cm was applied.