The Microstructure of Aluminide Coatings on 310S and 347H Steels Formed by Pack Aluminizing and Their Corrosion Behavior in Molten Chloride Salts
Weiqian Chen,Peiqing La,Zengpeng Li,Yaming Li,Lei Wan
DOI: https://doi.org/10.3390/coatings14121507
IF: 3.236
2024-12-01
Coatings
Abstract:In order to enhance the resistance of superalloys to high-temperature molten chloride salt corrosion, Fe-Al coatings were prepared on 310S and 347H stainless-steel surfaces via pack aluminizing. Then, the coatings were annealed at different temperatures to explore the influence of temperature on their phase constitution, microstructure, microhardness, and corrosion resistance. The results showed that the annealing temperature had a considerable effect on the corrosion resistance of the Fe-Al coatings, which was related to the change in the phase composition of the coatings that occurred due to the annealing treatment. The growth rate of the coating on 347H steel was higher than that on 310S steel, and their thicknesses from aluminizing at 800 °C for 20 h were 209.6 and 153.5 μm, respectively. When annealing at 900 °C for 30 h, the phase composition of the coatings was completely transformed into (Fe, Cr, Ni) Al. The corrosion loss rate of the annealed coating was clearly reduced, the loss rate of the 310 coating was 6.0 and −0.25 mg/cm2 before and after annealing at 900 °C and that of the 347 coating was 4.89 and −0.7 mg/cm2 before and after annealing at 750 °C, respectively. The two coatings showed good corrosion resistance to molten chloride salts, as demonstrated by the oxide scale (Al2O3) that formed on the surface, which had a thickness of about 30~40 μm.
materials science, multidisciplinary,physics, applied, coatings & films