Effects of Alloy Elements on Corrosion Resistance of Fe-based Stainless Steels in Molten NaCl

Wang Junwei,Wang Zhiping,Lu Yang,Cheng Bo,Li Wensheng,Dong Hongfeng
2013-01-01
Rare Metal Materials and Engineering
Abstract:In order to develop thermal storage chamber material for NaCl high temperature phase change medium, average mass loss rate was compared among five kinds of Fe-based stainless steals with different mass fractions of Cr, Ni, Ti and Mo after corroded in 850 degrees C molten NaCl for 168 h. Corrosion products on specimens surface and composition of corrosion residual molten salt were detected by X-ray diffraction (XRD). Cross section morphology and variation tendency of elements content near corrosion layer were studied by scanning electron microscopy (SEM)/X-ray energy dispersive spectrometry (EDS) and electron probe micro-analyzer (EPMA). Effects of four elements (Cr, Ni, Ti and Mo) on corrosion resistance performance of Fe-based alloy were analyzed. Results show that there are no firmly attached metal oxides on corroded specimens surface and only marginala TiO2 exists in corrosion residual molten salt besides NaCl. Cr is the primary cause of specimen mass loss. Corrosion resistance of the alloy will be improved by increasing mass fraction of Ni. But corrosion process will be accelerated by adding Ti to alloy. Loose shell that inhibits corrosion process is formed on the surface of corroded specimens containing Mo.
What problem does this paper attempt to address?