Effect of QLT process on microstructure and properties of new axle steel

HUANG Xi,SHANGGUAN Changping,WANG Zemin,WANG Lianbo,LIU Min,ZHANG Cheng,WANG Zhanyong

DOI: https://doi.org/10.3969/j.issn.2097-017X.2022.05.005

2022-01-01

Abstract:The effect of the quenching intercritical quenching and tempering（QLT）process on the lowtemperature toughness of high-speed train axle steel is studied by the scanning electron microscopy（SEM）,X-ray diffraction（XRD）,tensile test,and impact test. The results show that with the increase of the holding time in the two-phase zone,the yield strength of the sample steel decreases first and then increases,while the elongation increases first and then decreases. When the holding time in the two-phase zone is constant,the yield strength and elongation of the sample steel still maintain this trend with the increase of tempering temperature. Under the QLT process,more stable reversed austenite can be obtained after held in the two-phase region at 700 ℃ for 1 h and then heated to 550 ℃ for30 min. This sample steel exhibits the optimal low-temperature toughness,with its impact toughness of 1325 kJ/m~2at room temperature,yield strength of 797 MPa,and elongation of 20.25%. Furthermore,its impact toughness still reaches 1149 kJ/m~2at-80 ℃.