Impact Toughness and Fractography of Equiaxed/Columnar Heterogeneous Microstructure in Al-Cu Alloy Fabricated by Arc-Directed Energy Deposition

Yinghui Zhou,Zhennan Wang,Xin Lin,Zengyun Jian,Yongqin Liu,Yongming Ren,Tianchi Zhang,Wenting Shao,Xigang Yang

DOI: https://doi.org/10.2139/ssrn.4250819

2022-01-01

SSRN Electronic Journal

Abstract:To improve the dynamic impact toughness of Al-Cu alloys with equiaxed/columnar heterogeneous microstructures were fabricated via several methods. They were fabricated using arc-directed energy deposition (Arc-DED), as well as the deformation and fracture mechanism under the dynamic impact loading of air cooling (AC), water cooling (WC), hot isostatic pressing (HIP), and heat treatment (T6). The samples were systematically investigated using instrumented Charpy impact tests, which are critical for Arc-DED-processed Al-Cu alloys applied in damage tolerance structures and dynamic loading conditions. Analysis of the load-displacement curves reveals that the impact absorbed energy of the WC/HIP/T6 sample was 2.24, 1.91, and 2.79 J for WC, HIP, and T6, respectively, which is significantly higher than that of the AC sample (1.21 J). Interestingly, the crack formation energy values among the AC,WC,HIP,T6 samples are similar (0.47/0.57/ 0.62/0.64 J for AC/WC/HIP/T6). However, the higher crack propagation energy of the WC/HIP/T6 (1.67/1.28/2.15 J) samples than that of the AC (0.74 J) sample indicates a better resistance to crack propagation in WC/HIP/T6 than AC samples. The dynamic impact load is significantly different from the static load tensile load, and the geometrically necessary dislocation (GND) density of the dynamic impact is relatively uniform in the equiaxed and columnar grains, unlike the GNDs concentrated in the columnar grain zones during the static tensile load. Brittle fractures with inhomogeneous dimples were observed in all the samples. The key determinant of the impact toughness was the block-shaped brittle θ phase that precipitated along the grain boundaries and pore defects. Therefore, the impact toughness of the WC sample with a low-volume fraction θ phase precipitated at equiaxed grains, HIP sample with low porosity, and T6 sample with a large amount of ductile θ″ phase were significantly improved. This study not only provides valuable insights into the dynamic fracture resistance of Arc-DED-processed Al-Cu alloys but also elucidates the effects of equiaxed/columnar grain morphology, precipitates, and pore defects on the deformation and fracture mechanism under dynamic impact loading.