Inhibiting Migration/Loss of Iodide Ions by Lock-Like Interaction for Improving the Performance of Perovskite Solar Cells

Qingrui Cai,Yao,Yao Lu,Mingliang Wang,Yanqiu Zhang,dandan Song,Zheng Xu,Xiaodan Li,Dong Wei
DOI: https://doi.org/10.2139/ssrn.4160313
2022-01-01
SSRN Electronic Journal
Abstract:Iodide ions (I - and I 3 - ) in perovskites are tend to migration resulting in the phase segregation and degradation of perovskite films and devices under illumination or operation conditions. In order to overcome this intrinsic difficulty, passivation and additive strategies have been developed in many works. Here, we introduced polyetheramine (PEA) into perovskite films to inhibit the migration and loss of iodides and suppress the defects related with these migrated ions. The perovskite films with PEA had barely iodide loss even under long-term ultraviolet (UV) illumination and possessed lower trap density compared with the pristine films no-mater before or after UV aging process. Density functional theory (DFT) calculation revealed that PEA can form strong interaction with iodides and Pb 2+ in perovskites through the Pb=O and H-I bonds, and the iodide ions (I - and I 3 - ) could be locked firmly by PEA preventing them to migration or loss. By using this method, the efficiency of perovskite solar cells (PSCs) had improved from 19.71 % (without PEA) to 22.02 % (with PEA). After 200 min of maximum power point (MPP) tracking, the efficiency of PSCs with PEA remained 89 % of its initial value and that of PSCs without PEA fully degraded.
What problem does this paper attempt to address?