Abstract:The construction of deeply buried tunnels has intensified concerns regarding shrinkage cracking and the long-term performance deterioration of lining concrete in dry-hot environments. These issues are related to the dynamic interconversion of internal moisture states, the changing moisture behavior over time, and the evolution of calcium silicate hydrate (C-S-H) properties. However, the mechanisms underlying these phenomena are not fully understood. This study investigates the dynamics of moisture content across different states, the source and composition of evaporated water, as well as the mechanism of change in the microscopic properties of C-S-H in concrete subjected to dry-hot conditions (40°C and 60°C) and standard curing environments through tests on water loss rates, chemically bound water, and low-field nuclear magnetic resonance. The findings reveal that at 40°C and 60°C, hydration products were generated rapidly before mold removal, leading to significant increases in chemically bound water, interlayer water, and gel water, while capillary water was notably consumed. After mold removal, the rate of chemically bound water increase slowed, while interlayer water, gel water, and capillary water evaporated significantly, with gel water comprising 87.27 % and 83.51 % of the evaporated water at 40°C and 60°C, respectively. From day 1 to day 28, interlayer water, gel water, and capillary water contents decreased significantly, with reductions of up to 85.98 % at 60°C. In dry-hot environments, moisture primarily exists as chemically bound water and gel water, contrasting with standard curing conditions where capillary water is also present. The study concludes that drying of C-S-H gels leads to both positive effects, such as interlayer space compression and increased indentation modulus, and negative effects, including increased microporosity and reduced matric densification, ultimately contributing to the deterioration of long-term mechanical properties.

The volume stability of cement-based materials under different extreme environments in the plateau: Experimental evolution

Volume Stability of High Performance Concrete

Investigation of early drying shrinkage of ultrahigh-performance concrete under windy conditions

Experimental study on new variety of cement-stabilized soil

Micro-structure and Macro-performance: Surface Layer Evolution of Concrete under Long-term Exposure in Harsh Plateau Climate

Experimental study on early shrinkage and later expansion of concrete under a simulated geothermal environment

Time-varying moisture characteristics and C-S-H gel properties of concrete in dry and hot environments

Water Retention Behavior and Shear Strength of Artificially Cemented Granite Residual Soil Subjected to Free Drying

Experimental Investigation on the Strength and Microscopic Properties of Cement-Stabilized Aeolian Sand

Investigations on the Environmental Characteristics and Cracking Control of Plateau Concrete

Volume Changes and Mechanical Properties of Expansive Mudstone below Canals under Wet-Dry/Wet-Dry-Freeze-Thaw Cycles

Experimental Investigation on the Effect of High-Pressure Water on Tensile Strength and Microstructure of Cementitious Materials

Microstructures and Properties of Concrete Surfaces under Different Exposure Conditions in Complex Natural Environments of High-Altitude Regions

Impact of Wetting and Drying Cycles on the Mechanical Properties and Microstructure of Vegetation-growing Concrete

Effects of Mixed with Fly Ash and Slag Powder on Volume Deformation of Cement Mortar Under the Environment of Invariable Temperature and Variable Humidity

Physical Properties and Hydration Characteristics of Low-Heat Portland Cement at High-Altitude

Development of Pore Pressure in Cementitious Materials under Low Thermal Effects: Evidence from Optimization of Pore Structure by Incorporation of Fly Ash

Study on Mechanical and Microscopic Properties of Fly Ash Cement-Based Materials in High Geothermal Environment

Hydration and pore structure characteristics of concrete incorporating internal curing materials in a dry and large-temperature-difference environment

Experimental Study on Strength Characteristics of Cement Solidification Soil

Effect of low air pressure on the durability of concrete