Preparation and properties of an interpenetrating network polymer based on polydicyclopentadiene and phenolic resin
Weicheng Yang,Guibao Hu,Song Guo,Xinfeng Qiao,Yong Luo,Haiyan Ma
DOI: https://doi.org/10.1177/09540083221094725
IF: 1.73
2022-04-19
High Performance Polymers
Abstract:In this paper, phenolic resin (PF) and dicyclopentadiene (DCPD) monomers were mixed in different proportions. Under the action of a new generation of ruthenium carbene catalysts, DCPD was polymerised in situ. Polydicyclopentadiene (PDCPD)/PF interpenetrating polymer networks (IPNs) were prepared using the casting curing moulding process. The structure and properties of the prepared IPNs were characterised using Fourier infrared spectroscopy (FT-IR), apparent crosslinking degree, thermal weight loss, mechanical properties, impact resistance and scanning electron microscopy (SEM). The study results showed that the conversion of DCPD did not change with the addition of PF. But when its content exceeds 10%, the crosslinking degree of PDCPD decreases. When the PF content is 10%, the maximum bending strength of PDCPD/PF IPNs is (104.5 ± 1.3) MPa, maximum tensile strength is (74.5 ± 1.4) MPa, and maximum-notched impact strength is (4.2 ± 0.2) kJ/m 2 . Compared with PDCPD, the bending strength is increased by 22.7%, tensile strength is increased by 32.6%, and notched impact strength is increased by 31.3%, but the thermal stability has no major impact at this time. PF has good dispersibility and compatibility in DCPD. Due to the interpenetrating network structure of PF and PDCPD, the interpenetrating interlocking of the PF molecular chain and PDCPD crosslinked network restricts its movement. Its performance reached the optimum, and the PDCPD/PF IPNs with excellent performance was successfully prepared.
polymer science