Abstract:Laser shock peening (LSP), an innovative surface treatment technique, generates compressive residual stress on the surface of metallic components to improve their fatigue performance, wear resistance and corrosion resistance. To illustrate the dynamic response during LSP and residual stress fields after LSP, this study conducted FEM simulations of LSP in a Ti6Al4V alloy. Results showed that when power density was 7 GW cm(-2), a plastic deformation occurred at 10 ns during LSP and increased until the shock pressure decayed below the dynamic yield strength of Ti6Al4V after 60 ns. A maximum tensile region appeared beneath the surface at around 240 ns, forming a compressive-tensile-compressive stress sandwich structure with a thickness of 98, 1020 and 606 mu m for each layer. After the model became stabilized, the value of the surface residual compressive stress was 564 MPa at the laser spot center. Higher value of residual stress across the surface and thicker compressive residual stress layers were achieved by increasing laser power density, impact times and spot sizes during LSP. A 'Residual stress hole' occurred with a high laser power density of 9 GW cm(-2) when laser pulse duration was 10 ns, or with a long laser pulse duration of 20 ns when laser power density was 7GW cm(-2) for Ti6Al4V. This phenomenon occurred because of the permanent reverse plastic deformation generated at laser spot center.

Potential Residual Stress Control Strategies in Laser Shock Processing Via the Shaping of Laser Pulse Time Profiles

Influence of the Laser Pulse Time Profile on Residual Stress Characteristics in Laser Shock Peening

Study on Residual Stress of Laser Shock Processing Based on Numerical Simulation and Orthogonal Experimental Design

Laser Parameters in Laser Shock Processing:Research Progress and Prospect

Stepwise varying of laser parameters to enhance the residual stress field in multiple laser shock processing: numerical verification of single-point region

Optimization Of Residual Stresses Induced By Multiple Laser Shock Processing

Investigation on the non-homogeneity of residual stress field induced by laser shock peening

An Analytical Model To Predict Residual Stress Field Induced By Laser Shock Peening

Simulation of the elasto-plastic response and residual stresses near metal surface due to laser shock processing

Methods for the suppression of “residual stress holes” in laser shock treatment

Study on the Correlation Between External Plasma Plumes and Stress Distribution Inside a Target Immediately after Surface Laser Loading

Experimental and numerical investigation on residual stress of 316L SS treated by different laser shock peening parameters

Simulation And Experimental Study On Residual Stress Distribution In Titanium Alloy Treated By Laser Shock Peening With Flat-Top And Gaussian Laser Beams

Mitigation of Tensile Residual Stress Induced During Welding with Laser Shock Processing

Study on numerical simulation of residual stresses induced by laser shock processing

Unraveling Residual Stress Distribution Characteristics of 6061-T6 Aluminum Alloy Induced by Laser Shock Peening

Residual Stress Distribution and Microstructure at a Laser Spot of AISI 304 Stainless Steel Subjected to Different Laser Shock Peening Impacts

The Spatio-Temporal Evolution of Shock Wave Pressure Induced by Laser: Effects of Laser Parameters and Confinement Layer

Numerical Simulation of Residual Stress Field for Laser Shock Processing

Dynamic Response and Residual Stress Fields of Ti6al4v Alloy under Shock Wave Induced by Laser Shock Peening

Progress in applications of shockwave induced by short pulsed laser on surface processing