Influence of Temperature and pH Value in 3.5% NaCl Solution on Electrochemical Performance of 316L Stainless Steel

Wang G.,Zou Z. K.,Zhang P.,Wu Y.,Kou L. Y.,Xu Y. Q.

DOI: https://doi.org/10.1007/978-981-19-1457-7_35

2022-01-01

Abstract:Using potentiodynamic polarization, AC impedance and Mott-Schottky curve measurement methods, the electrochemical behavior and passivation characteristics of 316L stainless steel in 3.5% NaCl solution were studied. The experimental research results show that: The passivation film on the sample surface is relatively stable in the low-temperature alkaline solution. As the temperature of the solution increases and the pH decreases, the pitting potential of 316L stainless steel decreases accordingly, the corrosion current density increases, and the passivation interval decreases; The donor concentration and acceptor concentration near the surface oxide film increase; The change trend of electrochemical impedance spectroscopy is obviously different, and the pitting corrosion resistance of stainless steel becomes worse.