Bonding mechanisms of carbon fiber-reinforced plastic/aluminum alloy interface during friction lap welding via silane coupling treatment
C.Y. Jiang,L.H. Wu,F.C. Liu,P. Xue,B.L. Xiao,D.R. Ni,Z.Y. Ma
DOI: https://doi.org/10.1016/j.jmrt.2024.02.026
IF: 6.267
2024-02-18
Journal of Materials Research and Technology
Abstract:Silane coupling pretreatment could usually increase the strength of metal/plastic-based material joints, however, the detailed chemical bonding mechanism has not been clarified so far, which has become a key bottleneck for the further expanding application of this technology. Here, a specially designed silane coupling treatment was conducted on the aluminum alloy surface, and a strong friction lap welding (FLW) joint of carbon fiber-reinforced thermoplastic (CFRTP) to aluminum alloy was obtained. The average tensile shear force of 6.83 kN (∼30.36 MPa) was obtained, approximately 140% higher than the untreated joint, which was higher than the results obtained via FLW ever reported. The detailed bonding mechanism at the interface was studied by high-resolution transmission electron microscopy, x-ray photoelectron spectroscopy, and Fourier transform infrared reflection. It was found that the coupling agent layer observed at the interface acted as a bridge to achieve a tight bond with aluminum alloy and CFRTP. The bonding between the coupling agent layer and the aluminum alloy was achieved via the Si– O –Al and Si– O –Mg bonds, and the covalent bonding of C(=O)–N was formed by the chemical reaction between the CO bonds of CFRTP and the amino groups (-NH 2 ) of the coupling agent layer, resulting in the tight joining at the atomic scale. These chemical bonds contributed to the joint strength, which provided a better understanding of the joining mechanisms of plastic-based materials to metals via silane coupling treatment.
materials science, multidisciplinary,metallurgy & metallurgical engineering