Abstract:This paper presents an investigation on the thermal damage characteristics and mechanism of carbon fiber reinforced polymer (CFRP) during fiber laser joining between CFRP and mild steel with Cr electroplating. The results show that laser heat causes non uniform thermal damage of CFRP at the bonding interface. In the center region of the fracture after shear testing of the joint, CFRP endures serious ablation characterized with the formation of large cavities and the joint failure happens at the bonding interface. In the peripheral region of the fracture, a large amount of micron porosities are observed and the joint failure happens at the porosity zone in CFRP. According to the thermochemical analysis of CFRP, the critical temperatures of resin matrix decomposition, carbon residue oxidation and carbon fiber oxidation are 350°C, 484°C and 650°C respectively. When the temperature is higher than 350°C, the resin matrix of CFRP decomposes, producing gaseous products such as CO2, NH3 and the water vapor, which form the porosities in CFRP. When the temperature is higher than 484°C, the residual carbon is oxidized and ablation happens. The thermal histories at different locations of bonding interface show that Gaussian distribution of the laser beam results in nonuniform temperature distribution in the bonding interface. The peak temperature in the center of bonding interface is 654°C,higher than the CFRP oxidation temperature. CFRP in this region endures severe thermo-oxidation ablation. In the peripheral region of the bonding interface, the peak temperature drops from 484°C to 350°C sharply with the increase of distance from the center line and CFRP in this region endures decomposition. Through strict control of laser heat input, the thermal ablation can be completely eliminated and the amount of the porosities can be reduced. Thus the shear strength of the joint is apparently improved from 16.8MPa to 27.2MPa.Therefore, using the laser with uniform intensity distributioninstead of fiber laserand controlling the temperature of interface lower than CFRP decomposition temperature is a promising approach to suppress the thermal damagein CFRP.

Improvement of the Laser Joining of Cfrp and Aluminum Via Laser Pre-Treatment

Evaluation of the CFRP grafting and its influence on the laser joining CFRP to aluminum alloy

Influence of process parameters on the joint characteristics during laser joining of aluminium alloy and CFRTP

Effect of anodizing pretreatment on laser joining CFRP to aluminum alloy A6061

Optimization of microstructural morphology via laser processing to enhance the bond strength of Al-CFRP

Experimental and Theoretical Investigation of Laser Pretreatment on Strengthening the Heterojunction Between Carbon Fiber Reinforced Plastic and Aluminum Alloy.

Investigation on the joining process and strength of laser circle welding between Al5052 and CFRP dissimilar materials

Laser Direct Joining of CFRTP and Aluminium Alloy with a Hybrid Surface Pre-Treating Method

Investigation of laser joining process of CFRTP and aluminum alloy

Influence of laser texturing on the properties of fusion joints between aluminum alloys and carbon fiber reinforced thermoplastic composites

Enhancing Bond Strength Between Carbon Fiber Reinforced Thermoplastic and Aluminum Alloys Through Laser Surface Treatment

Effect of Interface Pretreatment of Al Alloy on Bonding Strength of the Laser Joined Al/CFRTP Butt Joint.

Effect of beam shaping on laser joining of CFRP and Al-Li alloy

Achieving a Strong Friction‐Lap Joint of Continuous Carbon‐Fiber‐Reinforced Plastic/Aluminum Alloy via a Surface Laser‐Processing Pretreatment

Joining of Aluminum and CFRP via Laser Powder Bed Fusion: Influence of Experimental Set-Up and Laser Processing on Microstructure and Mechanical Properties

Effect of Laser Micro-Texturing on Laser Joining of Carbon Fiber Reinforced Thermosetting Composites to TC4 Alloy

Suppression of Shrinkage Porosity in Laser-Joining of CFRP and Steel Using a Laser Surface Modification Process “Surfi-Sculpt ®”

The damage characteristics and mechanism of CFRP during laser joining of CFRP/mild steel dissimilar joint

Nanosecond laser ablation for improving the strength of CFRTP and aluminum alloy adhesively bonded joints

Influence of processing parameters on joint shear performance in laser direct joining of CFRTP and aluminum alloy

Effect of laser textured patterns on the interfacial characteristics and mechanical properties of 6061Al/GFRTP joints via hot-pressing