Influence of process parameters on the joint characteristics during laser joining of aluminium alloy and CFRTP

Ziwei Feng,Guolong Ma,Jianhui Su,Caiwang Tan,Xiaohui Han,Hongyun Zhao,Bo Chen,Xiaoguo Song

DOI: https://doi.org/10.1016/j.jmapro.2021.03.006

IF: 5.684

2021-04-01

Journal of Manufacturing Processes

Abstract:<p>Fiber laser joining of 6061 aluminium alloy and carbon fiber reinforced thermoplastic composite (CFRTP) was performed in this work. The effect of three process parameters including laser power, traveling speed and defocus distance on the bonding interface and joint properties was investigated. Shear tests were performed to evaluate the joint strength in different variables. X-ray photoelectron spectroscopy (XPS) was adopted to confirm the chemical states of elements at the interface. The results indicated that the shear strength of joints first increased and then decreased with the increase of heat input. Insufficient flow of CFRTP could not fill the grooves of aluminium alloy surface at low heat input. The resin was decomposed at excessisvely high heat input, causing pores remained at the interface. The fracture mode was determined as the interface failure. XPS result revealed that no new chemical bond was found at the interface, and the mechanical interlocking between aluminium alloy and CFRTP was main bonding mechanism. The maximum shear strength was 23.8 MPa, which was obtained as laser power, traveling speed and defocus distance was 1100 W, 5 mm/s and +10 mm, respectively.</p>

engineering, manufacturing

What problem does this paper attempt to address?

The paper aims to study the application of laser welding technology in the connection of aluminum alloy (6061) and carbon fiber reinforced thermoplastic composites (CFRTP), and to explore the impact of different process parameters on the performance of welded joints. Specifically, the paper focuses on the following issues:

1. **Impact of Process Parameters**:
- The study investigates the effects of three main process parameters: laser power, travel speed, and focal distance on the performance of the joints.
- It analyzes how these parameters influence the shear strength of the joints and the interface bonding conditions.

2. **Joint Performance Evaluation**:
- Shear tests are conducted to evaluate the shear strength of the joints under different process parameters.
- X-ray photoelectron spectroscopy (XPS) is used to analyze the chemical state of interface elements to confirm whether new chemical bonds are formed.

3. **Interface Bonding Mechanism**:
- The main bonding mechanisms between aluminum alloy and CFRTP are explored, and it is found that mechanical interlocking is the primary bonding method.
- The study examines the impact of resin flow and decomposition under different heat input conditions on the interface bonding.

Through the above research, the paper aims to find the optimal combination of process parameters to achieve high-strength aluminum alloy and CFRTP welded joints. The experimental results show that when the laser power is 1100 W, the travel speed is 5 mm/s, and the focal distance is +10 mm, the maximum shear strength of the joint reaches 23.8 MPa.