Enhanced cycling performance of lithium-ion batteries with V2O5 as cathode by Co-doping for structural stability

Baohe Yuan,Xiang Yuan,Zheng An,Binger Zhang,Shijun Luo,Lulu Chen,Xiansheng Liu

DOI: https://doi.org/10.1007/s10800-023-02050-3

IF: 2.925

2024-02-02

Journal of Applied Electrochemistry

Abstract:The high capacity and cycling performance are important for the lithium-ion battery (LIB). V 2 O 5 is considered a good active material among various potential candidates due to its low cost, abundant availability, and high energy density, however, the disadvantage of lower cycling performance is difficult to solve due to structural instability during the charging and discharging process. Here, we prepared composite microspheres of Co-doped V 2 O 5 by a simple solvothermal method for solving structural instability. As the cathode material in LIBs, the V 2 O 5 -Co 0.1 composite microspheres exhibit a specific capacity of 171 mAhg −1 at a current density of 0.08 Ag −1 (except for the first cycle). After 10 cycles, the specific capacity of V 2 O 5 -Co 0.1 composite microspheres did not change, it exhibited better cycling stability. When the current density is increased to 0.1 Ag −1 and 0.3 Ag −1 , 241 mAhg −1 and 200 mAhg −1 specific capacities are obtained. Although the initial specific capacity of pure V 2 O 5 microspheres was higher than that of V 2 O 5 -Co 0.1 , its capacity retention after cycling was 86%, which was lower than that of V 2 O 5 -Co 0.1 . The reason for the enhanced stability of V 2 O 5 -Co 0.1 composite microspheres is that Co ions are fixed between the layered structures of V 2 O 5 , which increases the stability of the V 2 O 5 structure.

electrochemistry