Abstract:CePO4 was prepared using the co-precipitation method. Recognizing the bifunctional nature of hetero-polyacid (salt), with both acidic and redox properties, it was modified by using phosphotungstic acid (HPW), and the HPW/CePO4 catalysts were synthesized using the impregnation technique. Various advanced techniques were employed to investigate aspects such as catalytic activity, microstructure, surface properties, and reaction mechanisms. These methods included NH3-SCR, XRD, XPS, SEM, BET, NH3-TPD, H2-TPR, and In-situ DRIFTs. Experimental findings indicated that the HPW-modified CePO4 catalysts exhibited enhanced SCR activity. Among them, the reaction activity window for NO x conversion of the W: Ce 0.05 catalyst was found to be 300∼400 °C, which represented the best activity temperature window. Following the incorporation of HPW, the HPW/CePO4 catalysts demonstrated an increased presence of Brønsted acidic sites, which concurrently led to a significant reduction in SO2 adsorption. The W: Ce 0.05 catalyst possessed the highest ratios of Oα/(Oα+Oβ+Oγ) and Ce4+/(Ce3++Ce4+). These ratios effectively regulated the sequestration and release of reactive oxygen species, thereby enhancing the activation of NH3. Consequently, this promoted the catalyst's low-temperature NH3-SCR reactivity. Lastly, the reaction process was examined using in-situ DRIFTs. The study revealed the generation of -NH2 intermediates at the Lewis acid sites of the W: Ce 0.05 catalyst. These intermediates subsequently underwent reactions with gaseous NO via the Eley-Rideal mechanism. This approach not only amplified the low-temperature catalytic efficacy of the catalysts but also bolstered their resilience to SO2, thereby fostering the long-term stability of the NH3-SCR reaction.

Balancing Acid and Redox Sites of Phosphorylated CeO2 Catalysts for NOx Reduction: the Promoting and Inhibiting Mechanism of Phosphorus.

Mnox/Ceo2/Sio2 Catalysts Prepared by Adsorption Phase Reaction Technique for Selective Catalytic Reduction of Nox at Low-Temperature

The Promoting Effects of Amorphous CePO 4 Species on Phosphorus-Doped CeO 2 /tio 2 Catalysts for Selective Catalytic Reduction of NO X by NH 3

Design Strategies for P-containing Fuels Adaptable CeO2-MoO3 Catalysts for DeNO(x): Significance of Phosphorus Resistance and N2 Selectivity.

High-Performance Strategy and Degradation Mechanism of Cezrvox Catalysts for Nox Reduction

The Poisoning Effects of Phosphorus on Ceo2-Moo3/Tio2 Deno(X) Catalysts: Nh3-Scr Activity and the Formation of N2o

Interaction of Phosphorus with a FeTiOx Catalyst for Selective Catalytic Reduction of NOx with NH3: Influence on Surface Acidity and SCR Mechanism

Influence of phosphorus on the NH3-SCR performance of CeO2-TiO2 catalyst for NOx removal from co-incineration flue gas of domestic waste and municipal sludge

Effects of phosphorus modification on the catalytic properties and performance of CuCeZr mixed metal catalyst for simultaneous removal of CO and NOx

Superior PbO-resistance of CeO2/ZrO2 catalyst promoted by solid superacid SO42−/ZrO2 for selective catalytic reduction of NOx with NH3

Promoting Metal Oxides–zeolite Electron Interaction on MnCeOx/HY Catalyst for Boosting Nitrogen Oxides Reduction

Modification Effect of Pt on the Active Sites of Sulfated CeO 2 Nanorods for the Selective Catalytic Reduction of NO

Correction to “promoter Rather Than Inhibitor: Phosphorous Incorporation Accelerates the Activity of V2O5–WO3/TiO2 Catalyst for Selective Catalytic Reduction of NOx by NH3”

Promotional effects of phosphotungstic acid on CePO4 catalyst for the selective catalytic reduction of NO with NH3

New Understanding of the Promotional Nature of SO2 on Ce-Based Oxide Catalysts for Selective Catalytic Reduction of NO X with NH3

Activating low-temperature NH3-SCR catalyst by breaking the strong interface between acid and redox sites: A case of model Ce2(SO4)3-CeO2 study

Shape Dependence and Sulfate Promotion of CeO2 for Selective Catalytic Reduction of NO with NH3

Influence of Sulfation on CeO2-ZrO2 Catalysts for NO Reduction with NH3

Effect of metal elements doping on the CePO4 catalysts for selective catalytic reduction of NO with NH3

Revealing the Dynamic Behavior of Active Sites on Acid-Functionalized CeO 2 Catalysts for NO x Reduction

Effective Way To Control The Performance Of A Ceria-Based Deno(X) Catalyst With Improved Alkali Resistance: Acid-Base Adjusting