Effects of Pre-Strain and Aging Treatments on the Mechanical Property and Corrosion Resistance of the Spray Formed Ultra-High Strength Al-Zn-Mg-Cu Alloy
Xiangdong Wang,Qinglin Pan,Weiyi Wang,Zhiqi Huang,Jian Chen,Baiqing Pan,Xiong Liu
DOI: https://doi.org/10.1016/j.matchar.2022.112381
IF: 4.537
2022-01-01
Materials Characterization
Abstract:Mechanical property and corrosion resistance are essential performances in ultra-high strength Al-Zn-Mg-Cu alloys for the aerospace and weapon industries. In this study, the pre-strain and aging treatments were used to enhance such performances of the spray formed ultra-high strength Al-Zn-Mg-Cu alloy. After 2% pre-strain with peak aging (PA) and retrogression and re-aging (RRA) treatments, the ultimate tensile strength, yield strength, and elongation can reach to 774 MPa, 735 MPa, 10.7% and 774 MPa, 747 MPa, 9.4%, respectively. The coarser precipitates of the samples with 4% pre-strain can lead to the slight lower strength compared with the samples with 2% pre-strain. The proper combination of pre-strain and aging treatments can also effectively enhance the stress corrosion resistance of the studied alloy by the following reasons. First, the higher strain concentration degree and dislocation density introduced by pre-strain treatments have high internal energy and provide more stored energy for the growth of the passive film. Second, the spacing of grain boundary precipitates under double aging (DA) and RRA states is larger than that under PA state. The width of uniform precipitation free zone (PFZ) with 2% pre-strain is larger than that with 4% pre-strain. Third, after pre-strain treatments, the cracks perpendicular to the deformation direction can be produced in Al7Cu2Fe phase, which further breaks up such particles. According to the results of Kelvin probe microscopy, the Al7Cu2Fe phase with smaller dimension can obtain the lower difference of potential to Al matrix.