Pre-Aging Effect on the Formation of Ω Phase and Mechanical Properties of the Al-Cu-Mg-Ag Alloy
Puyou Ying,Changhong Lin,Zhiyi Liu,Song Bai,Vladimir Levchenko,Ping Zhang,Jianbo Wu,Tao Yang,Min Huang,Gang Yang,Meng Liu,Mengjia Li
DOI: https://doi.org/10.3390/met12071208
IF: 2.695
2022-01-01
Metals
Abstract:In the present work, different aging treatments were performed to investigate the pre-aging effect on the formation of Ω phase and mechanical properties in Al-Cu-Mg-Ag alloy. The results showed that pre-strain could inhibit the formation of Ω phases, which was detrimental to the alloy strength. Due to the introduction of pre-aging treatment before pre-strain, the adverse effect of pre-strain on the precipitation of the Ω phase was reduced, and the alloy strength was increased by at least 15 MPa. Besides this, increasing the pre-aging temperature promoted the precipitation of Ω phases, inhibited the formation of θ′ phases, and improved the alloy strength. This was because the higher pre-aging temperature promoted more pre-precipitated Ω phases in the pre-aging process, and most of the pre-precipitated Ω phases could be retained and grew in the subsequent aging process. As a result, the tensile strength of the alloy increased from 523 MPa to 540 MPa. In addition, pre-aging with a higher temperature consumed more solute atoms, leading to less residual solute atoms in the matrix. Thus, the adverse effects of pre-strain, which inhibit the formation of clusters by the segregation of solute atoms, were reduced.