Abstract:Ti6Al4V (Ti64) alloys manufactured by selective laser melting (SLM) are well known for their susceptibility to failure at a low ductility of less than 10% due to the formation of an (α′) martensitic structure. Annealing and solution treatments as post-heat treatments of α′ are considered a good way to improve the mechanical performance of SLM-manufactured Ti64 parts. In this research, the effect of heat treatment parameters such as temperature (850 °C and 1020 °C) and cooling rate (furnace and water cooling) on the microstructure and mechanical properties of the SLM Ti64 structure was investigated. It was shown that the tensile strength/ductility of the Ti64 alloy produced by SLM was determined by the post-heat treatment. The experimental results revealed that heat treatment at 850 °C followed by furnace cooling resulted in the best possible combination of ductility (13%) and tensile strength (σy = 932, σu = 986 MPa) with a microstructure consisting mainly of 78.71% α and 21.29% β. Heat treatment at 850 °C followed by water cooling was characterized by a reduction in hardness and the formation of predominantly α plus α′′ and a small amount of β. HT850WC exhibited yield and tensile strengths of about 870 and 930 MPa, respectively, and an elongation at fracture of 10.4%. Heat treatment at 1020 °C and subsequent cooling in the furnace was characterized by the formation of an α + β lamellar microstructure. In contrast, heat treatment at 1020 °C and subsequent water cooling formed semi-equiaxial β grains of about 170 μm in diameter with longer elongated α grains and basket-weave α′. Post-treatment at 1020 °C followed by furnace cooling showed high ductility with an elongation of 14.5% but low tensile strength (σy = 748, σu = 833 MPa). In contrast, post-treatment at 1020 °C followed by water cooling showed poor ductility with elongation of 8.6% but high tensile strength (σy = 878, σu = 990 MPa). The effect of aging at 550 °C for 3 h and cooling in a furnace on the microstructure and mechanical properties of the specimens cooled with water was also studied. It was found that aging influenced the microstructure of the Ti6Al4V parts, including β, α, and α′′ precipitation and fragmentation or globularization of elongated α grains. The aging process at 550 °C leads to an increase in tensile strength and a decrease in ductility.

Anisotropy in the Tensile Properties of a Selective Laser Melted Ti-5Al-5Mo-5V-1Cr-1Fe Alloy during Aging Treatment

In-situ Investigation of the Anisotropic Mechanical Properties of Laser Direct Metal Deposition Ti6Al4V Alloy

Obtaining heterogeneous α laths in selective laser melted Ti–5Al–5Mo–5V–1Cr–1Fe alloy with high strength and ductility

In-situ Study of Microstructure and Mechanical Properties of GH3536 Alloy Manufactured by Selective Laser Melting at 750 °C

Aging responses of an Al-Cu alloy fabricated by selective laser melting

Heat-treatment induced microstructural evolution and enhanced mechanical property of selective laser melted near β Ti-5Al-5Mo-5 V-3Cr-1Zr alloy

Microstructure and Mechanical Properties of Ti-542 Alloy under Different Aging Designs

Multiple Α Sub-Variants and Anisotropic Mechanical Properties of an Additively-Manufactured Ti-6Al-4V Alloy

Effects of Aging Treatment on Microstructure Evolution and Mechanical Properties of Ti-6Al-3Nb-2Zr-Mo Alloy

Selective Laser Melting of Ti-5Al-2.5Sn Alloy with Isotropic Tensile Properties: the Combined Effect of Densification State, Microstructural Morphology, and Crystallographic Orientation Characteristics

Martensite decomposition during post-heat treatments and the aging response of near-α Ti–6Al–2Sn–4Zr–2Mo (Ti-6242) titanium alloy processed by selective laser melting (SLM)

The anisotropy of corrosion and passive behavior in selective laser melted Ti-5Al-5Mo-5 V-3Cr-1Zr alloy

Effects of Annealing and Solution Treatments on the Microstructure and Mechanical Properties of Ti6Al4V Manufactured by Selective Laser Melting

Enhanced Mechanical Properties of Ti-5Al-5Mo-5V-3Cr-1Zr by Bimodal Lamellar Precipitate Microstructures Via Two-Step Aging

Tensile Behavior of Ti-6Al-4V Alloy Fabricated by Selective Laser Melting: Effects of Microstructures and As-Built Surface Quality

In-situ investigation on the anisotropic behavior of the additively manufactured dual-phase Ti-6Al-4V alloy

A large compressive recoverable strain induced by heterogeneous microstructure in a Ni50.6Ti49.4 shape memory alloy via laser powder bed fusion and subsequent aging treatment

Mechanical Behavior Assessment of Ti-6Al-4V ELI Alloy Produced by Laser Powder Bed Fusion

Study of superior strength in Ti15Mo alloy manufactured using selective laser melting

Precipitation behavior and strengthening-toughening mechanism of hot rolled sheet of Ti65 titanium alloy during aging process

Influence of microstructural and crystallographic inhomogeneity on tensile anisotropy in thick-section Al-Li-Cu-Mg plates