The Effect of Neighboring Grain Orientation on Dislocation-Grain Interaction in Ti-5553 Alloy

Senzhen Wang,Shun Xu,Chongchen Xiang,Zijian Wang,Hanlin Ding
DOI: https://doi.org/10.1016/j.matchar.2022.112219
IF: 4.537
2022-01-01
Materials Characterization
Abstract:The accumulated dislocations are widely reported to be easily transmitted at low angle grain boundaries (GBs), while the associated mechanism at high angle GB needs further investigation. In this paper, the mechanisms associated with the interaction between GBs and < 111 > dislocations are investigated in Ti-5553 alloy with body-centered cubic structure. Slip traces transmitted into the neighboring grain or blocked by GBs are observed on the surface of the sample via secondary electron imaging. The corresponding slip system is determined with the combined use of EBSD-detected grain orientation and slip traces. The experimental results indicate that most slips can transfer at low angle GBs, while some slips can also transmit into the neighbor at high angle GBs. The misorientation angle of GBs is invalid to evaluate the mechanism induced by the interaction of dislocations with GBs. Crystallographic alignment-based analysis shows that slip transfer happens at GBs with favorable parameters of high geometric alignment (m') and low residual Burgers vector magnitude (vertical bar Delta b vertical bar). The general relation of GB misorientation angle with m' and vertical bar Delta b vertical bar is established. The results indicate that low angle GBs always possess high m' and low Delta b, while only some high angle GBs meet the requirement of large alignment parameters. This difference contributes to their preference of slip transfer. Finally, the orientations of best neighboring grains that are favorable for slip transfer are calculated, which is in agreement with the experimentally detected examples.
What problem does this paper attempt to address?