Abstract:Extreme thermal environment, especially transient high thermal load, is one of the great challenges for plasma facing tungsten materials. In this work, the fine-grained W-Y2O3 composites fabricated by nano in-situ composite method were exposed to transient heat loading using electron beams. The microstructure evolution, damage behavior and failure analysis were investigated by experimentally combing with finite element modelling (FEM). Besides, the correlation among thermal shock resistance, microstructure and mechanical properties of the W-Y2O3 composites were initially analyzed. Results show the W-Y2O3 composites obtains superfine microstructure and coherent interface. The surface morphology evolves from smooth to roughness, cracks and melting as the power density increases. Simultaneously, four crack patterns of surface micro-cracks, crack networks, longitudinal cracks and internal transverse cracks were observed. The W-0.3 wt%Y2O3 composites exhibit superior resistance to crack formation attributed to excellent interfacial performance and diffuse Y2O3 hindrance. No obvious damage was found on the surfaces when the power density reached 600 MW/m2. With the increasing Y2O3 contents, the thermal resistance of W-Y2O3 composites significantly decreases. Finite element modelling (FEM) analysis shows that the surface damage is the most serious compared to the interior after thermal shock. The damage, especially cracks, are preferentially formed on the surface, and then migrate and expand to the interior. The damage and its evolution are attributed to the palstic thermal strain on the surface caused by thermal stress. Moreover, the higher the mechanical properties of W-Y2O3 composites, especially the high temperature yield stress and elongation, the better high thermal load resistance. These results should be of relevance for the optimum design of W plasma facing materials in future nuclear fusion reactors.

Damage Characteristics of YAG Transparent Ceramics under Different Loading Conditions

Dynamic Response of YAG Polycrystalline and Single‐crystal Transparent Ceramics: Experiments and Mesoscopic Simulations

Dynamic behaviour of YAG transparent ceramic under ramp wave and shock compression loading up to 20 GPa

Damage Characteristics of Aluminum Nanorod under Hypervelocity Impact

Numerical modeling of dynamic response and microcracking in shock-loaded polycrystalline transparent ceramic

Microdamage In Polycrystalline Ceramics Under Dynamic Compression And Tension

Surface fracture behavior and subsurface damage of polycrystalline yttrium aluminum garnet ceramics in Vickers indentation

Determination of the Compressive Yield Strength for Nano-Grained YAG Transparent Ceramic by XRD Analysis

Surface Damage Evolution During Transient Thermal Shock of W-2%vol Y2O3 Composite Material in Different Surfaces

Dynamic response of a Li2O-Al2O3-SiO2 transparent glass-ceramic under shock compression

Dry sliding behavior of transparent yttrium aluminum garnet against 100Cr6 steel balls

Static and Dynamic Mechanical Properties of Yttrium Aluminum Garnet (YAG)

Dynamic Failure Behavior of Polycrystalline Alumina Under Impact Loading

Defects and solarization in YAG transparent ceramics

Surface Damage and Microstructure Evolution of Yttria Particle-Reinforced Tungsten Plate During Transient Laser Thermal Shock

Experimental and theoretical investigation of failure mechanism in Al 2 O 3 /SiC composite under plane shock waves

Spall Damage of a Ta Particle-Reinforced Metallic Glass Matrix Composite under High Strain Rate Loading

Nanoindentation and Nanoscratch Tests of YAG Single Crystals: an Investigation into Mechanical Properties, Surface Formation Characteristic, and Theoretical Model of Edge-Breaking Size

Mesoscopic Deformation Features of Shocked Porous Ceramic: Polycrystalline Modeling and Experimental Observations

The Microstructure Evolution, Damage Behavior and Failure Analysis of Fine-Grained W-Y2O3 Composites under High Transient Thermal Shock

Deformation Behaviors of A Tizrnicube Bulk Metallic Glass under Shock Loading