Abstract:The use of Ni-based catalysts is a common method for eliminating tar through catalytic cracking. Carbon deposition is the main cause of deactivation in Ni/ZSM-5 catalysts, with filamentous MWCNTs being the primary form of carbon deposits. This study investigates the formation and evolution of CNTs during the catalytic process of biomass tar to explore the mechanism behind carbon deposition. The effect of the 9Ni/10MWCNTs/81ZSM-5 on toluene reforming was investigated through a vertical furnace. Gases produced by tar catalysis were evaluated through GC analysis. The physicochemical structure, properties and catalytic performance of the catalyst were also tested. TG analysis was used to assess the accumulation and oxidation reactivity of carbon on the catalyst surface. An analysis was conducted on the mechanism of carbon deposition during catalyst deactivation in tar catalysis. The results showed that the 9Ni/91ZSM-5 had a superior toluene conversion of 60.49%, but also experienced rapid and substantial carbon deposition up to 52.69%. Carbon is mainly deposited as curved filaments on both the surface and pore channels of the catalyst. In some cases, tip growth occurs where both carbon deposition and Ni coexist. Furthermore, specific surface area and micropore volume are reduced to varying degrees due to carbon deposition. With the time increased, the amount of carbon deposited on the catalyst surface increased to 62.81%, which gradually approached saturation, and the overall performance of the catalyst was stabilized. This situation causes toluene molecules to detach from the active sites within the catalyst, hindering gas release, which leads to reduced catalytic activity and further carbon deposition. It provides both a basis for the development of new catalysts and an economically feasible solution for practical tar reduction and removal.

In Situ Study of Carbon Nanotube Formation by C2H2 Decomposition on an Iron-Based Catalyst

Study on Carbon Nanotubes of Pyrolysis Carbons P for In Situ Catalytic Formation on Expanded Graphite Surface

In Situ TEM Observation of the Gasification and Growth of Carbon Nanotubes Using Iron Catalysts

Carbon-Involved Near-Surface Evolution of Cobalt Nanocatalysts: an in Situ Study

A New Understanding of Carbon Nanotube Growth: Activation and Deactivation of a Catalyst

Catalyst-Free in Situ Carbon Nanotube Growth in Confined Space Via High Temperature Gradient

Mössbauer Study on the Conversion of Different Iron-Based Catalysts Used in Carbon Nanotube Synthesis

Pyrolytic Synthesis of Carbon Nanotubes on Ni, Co/MCM-41 Catalysts

Study of Controlled Growth of Carbon Nanotubes in Microstructures at Low Temperature

Carbon Nanotubes: in Situ Monitoring the Role of Working Metal Catalyst Nanoparticles for Ultrahigh Purity Single‐Walled Carbon Nanotubes (adv. Funct. Mater. 40/2013)

Preparation of High Purity Carbon Nano -Tubes from Ethylene Decomposition over Nanosized Iron- Based Catalysts

In Situ Carbon Nanotube Synthesis by the Reduction of NiO/γ-Al2O3 Catalyst in Methane

Characterization and Magnetic Properties of Helical Carbon Nanotubes and Carbon Nanobelts Synthesized in Acetylene Decomposition over Fe−Cu Nanoparticles at 450 °C

Preparation of Nanosized Iron Catalyst and Small Diameter Carbon Nanotubes from Methane Decomposition

In Situ X-ray Raman Scattering Spectroscopy of the Formation of Cobalt Carbides in a Co/TiO2 Fischer–Tropsch Synthesis Catalyst

In Situ Characterization of Cu/CeO2 Nanocatalysts for CO2 Hydrogenation: Morphological Effects of Nanostructured Ceria on the Catalytic Activity

Confinement in Carbon Nanotubes and Its Catalytic Application

The Effect of Hydrogen on the Formation of Nitrogen-Doped Carbon Nanotubes Via Catalytic Pyrolysis of Acetonitrile

A Comparison Study of Catalytic Oxidation and Acid Oxidation to Prepare Carbon Nanotubes for Filling with Ru Nanoparticles

Study on the mechanism of carbon nanotube-like carbon deposition in tar catalytic reforming over Ni-based catalysts

Catalytic Decomposition of CH4 to Hydrogen and Carbon Nanotubes Using the Pt(1)-Fe(30)/MCM-41 Catalyst