Ce–Fe–Mn Ternary Mixed-Oxide Catalysts for Catalytic Decomposition of Ozone at Ambient Temperatures
Xiao Chen,Zhenglong Zhao,Shuo Liu,Jinxing Huang,Jing Xie,Ying Zhou,Zhiyan Pan,Hanfeng Lu
DOI: https://doi.org/10.1016/j.jre.2019.01.010
IF: 4.632
2019-01-01
Journal of Rare Earths
Abstract:Ce-modified Mn-Fe mixed-oxide catalysts were prepared by a citric acid sol-gel method and characterized by X-ray diffraction, Raman, N-2 adsorption-desorption, infrared spectra, H-2 temperature-programmed reduction and thermogravimetric analyses. Their catalytic properties were investigated in ozone (O-3) decomposition reaction. Results show that the small amount of rare earth metal Ce added during Mn-Fe (FM) mixed-oxide synthesis greatly improves the catalytic performance in O-3 decomposition. Among the prepared catalysts, the C-0.04(FM)(0.96) mixed-oxide catalyst exhibits the highest catalytic activity and stability. The O-3 conversion over C-0.04(FM)(0.96 )is 98% after 24 h reaction at 25 degrees C under dry condition, and that over FM decreases to 90% after 16 h reaction. At 0 degrees C, the O-3 conversion over Ca-0.04(FM)(0.96) is 95% after 7 h reaction under dry condition, and that over FM slows down to 70%. Under humid condition (RH = 65%), the O-3 conversion over C-0.04(FM)(0.96) is 63% after 6.5 h reaction at 25 degrees C, while that over FM decreases to 55%. When Ce is doped into Mn-Fe mixed oxides, the small amount of Ce enters the crystal lattice of MnO2, and partial Fe is separated to form Fe2O3. This changes cause lattice distortion and increase defects and enable the as-synthesized Ce-Fe-Mn ternary mixed-oxide catalysts to acquire additional oxygen vacancies and increase their specific surface area, thereby increasing the number of reaction sites and enhancing the catalytic performance of the catalysts for O-3 decomposition. (C) 2020 Published by Elsevier B.V. on behalf of Chinese Society of Rare Earths.