Atomic Scale Investigation of FCC → HCP Reverse Phase Transformation in Face-Centered Cubic Zirconium

Wenbin Guo,Fuzhou Han,Geping Li,Yingdong Zhang,Muhammad Ali,Jie Ren,Qichen Wang,Fusen Yuan

DOI: https://doi.org/10.1016/j.jmst.2022.07.032

2023-01-01

Journal of Material Science and Technology

Abstract:Mechanism of FCC -> HCP reverse phase transformation in face-centered cubic zirconium (FCC-Zr) along with a concomitant 70.5 degrees rotation of alpha-Zr matrix were investigated in zircaloy-4 (Zr-4) cladding tube by using transmission electron microscopy (TEM). Results showed that the interaction among a secondary phase particle (SPP) and three FCC-Zr grains resulted in the formation of cross stacking faults in SPP and exerted a drag force on minor axis of the adjacent FCC-Zr phase. Moreover, when the shear stress along [1 1 2](FCC-Zr) direction was large enough to initiate the emission of 1/6 [1 1 2] Shockley partial dislocation on every other ( 111)FCC-Zr close-packed plane, the stacking sequence would change from ABCABCA to ABABABA viz. (0 0 01) planes of the daughter HCP phase. Thus, FCC -> HCP reverse phase transformation in FCC-Zr was presented. (C) 2022 Published by Elsevier Ltd on behalf of The editorial office of Journal of Materials Science & Technology.