Ultrastrong Nanocrystalline Oxide-Dispersion-strengthened Ferritic Alloy with Exceptional Thermal Stability
X. C. Cai,J. J. Liang,L. D. Xu,B. R. Sun,Z. Chen,K. K. Wen,S. B. Jin,G. Sha,T. D. Shen
DOI: https://doi.org/10.1016/j.msea.2021.141616
IF: 6.044
2021-01-01
Materials Science and Engineering A
Abstract:As structural materials candidates of advanced fission and future fusion reactors, oxide-dispersion-strengthened (ODS) alloys, which are often ultrafine-grained (with a grain size between 100 and 1000 nm), have attracted widespread interest in past decades. However, fabrication of fully dense bulk nanocrystalline ODS alloys has rarely been reported. In this work, a novel Zr-doped nanocrystalline 14YWTZ ferritic ODS alloy (Fe-14Cr-3W0.4Ti-0.8Zr-0.3Y(2)O(3)) was prepared by mechanical alloying and high-pressure consolidation techniques. The high consolidation pressure (4 GPa) endows the bulk nanocrystalline 14YWTZ alloy with a nearly full relative density (similar to 99.5%) and a reasonable tensile elongation. The consolidated nanocrystalline 14YWTZ alloy with an average grain size of similar to 50 nm shows an ultra-high compressive yield strength of similar to 2641 MPa. Besides, the alloy exhibits an exceptional thermal stability, i.e., limited grain growth occurs after annealing at a high temperature of 1000 degrees C. After hot rolling, the alloy retains nanocrystalline microstructures and exhibits an unprecedented tensile yield strength of 2730 MPa, far exceeding those of previous reported ferritic ODS alloys. The high thermal stability of the annealed nanocrystalline 14YWTZ alloys can be ascribed to the combined effects of the thermodynamic multicomponent co-segregation to grain boundaries and strong kinetic Zener pinning by highdensity Zr-Ti-Y-O-enriched nanoparticles with an average particle size of similar to 3.18 nm and a high number density of similar to 3 x 10(24) m(3). The outstanding strength of the present nanocrystalline 14YWTZ alloys primarily originates from the Hall-Petch strengthening of the nanocrystalline matrix, distinguishing them from conventional ODS alloys strengthened by dislocation forest and/or dispersed oxide nanoparticles.