Temperature-Stable X(na0.5bi0.5)moo4–(1–x)moo3 Composite Ceramics with Ultralow Sintering Temperatures and Low Dielectric Loss for Dielectric Resonator Antenna Applications
Shu-Zhao Hao,Di Zhou,Chao Du,Li-Xia Pang,Charanjeet Singh,Sergei Trukhanov,Alex Trukhanov,Antonio Sergio Bezerra Sombra,Jobin Varghese,Qiang Li,Xiu-Qun Zhang
DOI: https://doi.org/10.1021/acsaelm.1c00193
IF: 4.494
2021-01-01
ACS Applied Electronic Materials
Abstract:Fifth-generation mobile communication systems provide a huge market for microwave dielectric materials, especially in the manufacture of dielectric resonators, filters, substrates, and antennas. Herein, an excellent performance microwave dielectric ceramic x(NaBi)(0.5)MoO4-(1-x)MoO3 (0.2 <= x <= 0.9, abbreviated as xNBM-(1-x)MO sintered below 660 degrees C with two coexisting phases is prepared via a solid solution reaction. With the increasing x value, the sintering temperature rises from 600 to 640 degrees C. The dielectric properties have a series of changes with increasing permittivity (10.3-28.1), decreasing Q(f) value (12,080 to 8600 GHz), and increasing tau(f) value (-27.1 to +21.2 ppm/degrees C). Typically, at the ultralow temperature of 630 degrees C, the 0.8NBM-0.2MO ceramic exhibits great microwave performance with epsilon(r) similar to 24.4, Q(f) similar to 9030 GHz (7.7 GHz), and a near-zero tau(f) similar to 7.2 ppm/degrees C. A prototype dielectric resonator antenna is manufactured using a 0.8NBM-0.2MO ceramic. A high-impedance bandwidth similar to 360 MHz can be obtained in the antenna at 7.74 GHz with -10 dB transmission loss (S-11). Furthermore, the chemical compatibility with Al powder indicates that the xNBM-(1-x)MO composite ceramics may be promising microwave materials for applications in ultralow-temperature co-fired ceramic technology.