An investigation on the microstructure formation of polymer modified mortars in the presence of polyacrylate latex
Ye TIAN,LI Zong-jin,MA Hong-yan,Xian-yu JIN,Nan-guo JIN
2011-01-01
Abstract:In this research, the microstructure formation of polyacrylate (PA) latex modified mortars was investigated from mixing to hardening. The polymer film forming process was studied, with specific emphasis on the chemical and physical reactions between polymer and cement hydration products. An improved four-step model was proposed for representing the mechanism of polymer modification in view of the reactivity of polymer latex in cement-based materials. And the influence of PA latex on the microstructure formation of mortars was revealed through the analysis of pore structure and polymer distribution. Owing to cement hydration, the uniform dispersion of polyacrylate polymer in fresh mortar will be destructed, and polymer particles will deposit and flocculate into big groups at some local positions. The modification of polyacrylate polymer on cement-based materials is localized which can be stated as the localization of polymer modification. The addition of PA latex will also introduce some air voids into mortars due to the chemical reaction between its surfactant and cement hydrates. This is important for the physical and mechanical properties improvement because a kind of purposefully designed polymer latex will effectively enhance the performance of cement-based materials in a relative small dosage, which means cutting the cost down and broadening its application. 1 GENERAL INSTRUCTIONS Cement-based materials have now become the dominant construction materials for the civil infrastructure all over the world. The addition of a minor amount of polymer into a cement mix can significantly enhance the properties of the resulting material, which is known as a polymer modified cement-based material (Chung, 2004). In polymer modified cement-based material, polymer particles, unhydrated cement particles and cement hydration products will form a polymer-cement co-matrix together (Ollitrault-Fichet et al., 1998). The presence of the polymer particles will refine the pore structure, thereby decrease the porosity (Liu et al., 2003). Moreover, the polymer modified cement-based materials show a good workability and enhanced water retention. And, mechanically, the presence of polymer tends to increase the flexural strength and toughness (Sujjavanich and Lundy, 1998; Zhong and Chen, 2002). Owing to these superior properties, the polymer modified cement-based materials have already been widely used as the adhesive or finishing materials, and repair materials for reinforced concrete structures. Due to the rising importance of polymer modified cement-based materials in civil construction, many attempts have been made to clarify the mechanism of polymer modification (Sakai and Sugita, 1995; Su et al., 1996; Afridi et al., 2003; Wang et al., 2006). Among these researches, Ohama’s three-step model is taken as the most representative achievement in describing the formation of the polymer-cement co-matrix (Ohama, 1995). According to Ohama, the polymer particles firstly uniformly disperse in the cement paste. And the polymer particles deposit partially on the surfaces of the cement particles. As the cement hydration proceeds and the capillary water is consumed, the polymer particles flocculate to form a continuous close-packed layer on the surfaces of the cement-gel-unhydrated-cement particles mixtures. Finally, the closepacked polymer particles on the cement hydrates coalesce into continuous films, and the films bind the cement hydrates together to form a monolithic network in which the polymer phase interpenetrates throughout the cement hydrates phase. Taking Ohama’s model as a research base, some adjustments and refinements, in addition with several experimental works, are made to established an integrated model in which the reciprocal influences between the polymer and the cement particles are incorporated and implemented on a time scale (Beeldens et al., 2005; Gemert et al., 2005). However, in Ohama’s model, a continuous polymer film or an interpenetrative polymer network is indispensable for an effective modification and properties improvement of the polymer modified cement-based materials. But sometimes in cement-based materials, only scattered polymer films are found, especially for the polymer modified cement-based materials with a low polymer/cement (P/C) ratio (Afridi et al., 2003; Wang et al., 2005;). While the addition of small amounts of polymers (usually below 4%) also clearly influences the properties of the hardened materials. It is clear that there exist other morphologies of polymer materials other than continuous polymer films, and also other mechanisms of polymer modification, in a low P/C ratio. In this research, newly developed polyacrylate (PA) latex was used as the polymer admixture. A series of tests were carried out to simulate the chemical and physical reactions happened between polymer latex and cement particles in polymer modified mortars from mixing to hardening. The morphologies of the co-matrix were analyzed and identified. And a new model expanded from Ohama’s research on the mechanism of polymer modification was proposed based on the Scanning Electronic Microscope (SEM) and Energy dispersive X-ray detector (EDX) observations. 2 MATERIALS AND SAMPLES PREPARATION 2.1 Polyacrylate latex The PA latex used in this research is a kind of milky suspension which is stabilized by surfactant, sodium dodecyl sulfate (SDS). The diameter of PA particles ranges from 40nm to 200nm. And the mean diameter of PA particles is 80.2 nm. The molecule structure of PA is composed of a main chain and thousands of short side chains which can be classified according to their hydrophilic properties as anionic and nonionic. EDX analysis of PA polymer film states that its carbon/oxygen (C/O) ratio ranges from 1.5 to 3. While in concrete, the cement hydration products are all inorganic with C/O ratio close to 0. Even the carbonation of cement can only generate the chemical reaction products with the C/O ratio of 0.33 (CaCO3) which is much lower than that of PA polymer. So the value of C/O ratio, in this research, will be used to identify the trace of polymer modification in concrete. 2.2 Other raw materials Ordinary Portland cement (ASTM type I), with the density of 3.15 g/cm, was used in this study. The Blain specific area of cement is 3.85×10 cm/g. And the average particle size of Portland cement is 18.09μm. The size of quartz sand employed in this research ranges from 0.5mm to 3.1mm. The fineness modulus and relative density of quartz sand are 1.6 and 2.66 respectively. A milky alkali-resisting silicone antifoaming agent for concrete was applied to reduce the entrainment caused by the residual SDS in PA latex. The deionized water was used in this study. 2.3 Mix proportions and samples preparation Three kinds of PA modified mortars were employed in this research to investigate the mechanism of PA latex modification on cement-based materials. All mortar samples were prepared with a water/cement ratio of 0.5 and a sand/cement ratio of 2. Samples PA00, PA05 and PA10 represent the mortars with the P/C ratio of 0.00, 0.05 and 0.10, respectively. For the mortars modified with PA latex, 0.5% defoamer was added by weight of cement. All the samples were cured in standard curing conditions (95%RH and 25°C) for 3 days and a nature curing at ambient humidity and temperature (60%RH and 20°C) from 3d to 28d.