Abstract:Nickel base superalloys are widely used in the preparation of hot end parts for aircraft engines because of their good comprehensive mechanical properties, oxidation resistance and structural stability. It's strengthened mainly by solid solution strengthening, gamma' phase strengthening and carbide strengthening. High alloying is one of the main methods to improve the solid solution strengthening level of nickel base superalloys, where the element W is an efficient alloying element with low price. The control of the W content is extremely important for high W content nickel base superalloys. However, there are few reports on the influence of W content on the microstructure of high W alloy. According to this background, by means of OM, SEM observation and XRD analysis, the influence of W content on the solidified microstructure in nickel base superalloy have been investigated in this work. Results show that when the W content is about 14% (mass fraction, the same below), there is no alpha-W phase being precipitated in the alloy. While as the content of W is higher than 16%, alpha-W could be precipitated during the solidification. On another hand, the grain size of the alloy decreases from 1.04 mm to 0.17 mm and the volume fraction of eutectic increases from 6% to 10% with the increase of the W content. While the content of W has no obvious effect on the sizes and morphologies of gamma' phase in the dendrite and inter-dendrite areas. During solidification, the a-W phase will be first precipitated due to its higher precipitation temperature, and the shrinkage of the residual liquid phase may cause the shift and growth of the alpha-W to the core of the liquid phase. The alpha-W could be as the core of the heterogeneous nucleation to reduce the critical nucleation energy, which is the main reason that the grain size of the 18%W alloy is smaller. During the growth of the dendrites with various orientations, the concentration of Al and Ti in the residual liquid phase may have a higher concentration gradient to cause the occurrence of eutectic transformation, which is the main reason that there is a higher volume fraction of eutectic in 18%W alloy.

Effect of Ni Content on Solidification Behavior and Hot-Tearing Susceptibility of Co–Ni–Al–W-Based Superalloys

Effects of Al content on microstructures and high-temperature tensile properties of two newly designed CoNi-base superalloys

Effect of Ti and Ta content on the oxidation resistance of Co-Ni-based superalloys

High-throughput exploration of alloying effects on the microstructural stability and properties of multi-component CoNi-base superalloys

Mechanical Properties and Oxidation Characteristics of TiNiAl(Nb) Intermetallics

The Mechanical Properties of Intermetallic Ni50−xTi50Alx Alloys (X=6,7,8,9)

Effects of Cobalt on Solidification Characteristics and As-Cast Microstructure of an Advanced Nickel-Based Single Crystal Superalloys

Effect of Ta Addition on the Microstructure and Tensile Properties of a Ni-Co Base Superalloy

Effects of Alloying Elements on the Microstructure of Precipitation Strengthened Co-based Superalloys

Effect of Melt Superheat Treatment on Solidification Behavior and Microstructure of New Ni–Co Based Superalloy

Influence of W Content on the Microstructure of Nickel Base Superalloy with High W Content

The Evolution of Microstructure and Mechanical Properties at Elevated Temperature of Cast Al–Li–Cu–Mg Alloys with Ni Addition

Effect of Chromium Content on the Oxidation Behavior of a Ta Stabilized Γ’-Strengthened Polycrystalline Co-30Ni-10Al-4W-4Ti-2Ta Alloy

Influence of Co Content on the Microstructures and Mechanical Properties of a Ni–Co Base Superalloy Made by Specific Additive Manufacturing Process

Effect of Si on the Solidification Segregation Behavior of a New Ni–Co‐Based Superalloy

The Temperature Dependence of High-Temperature Strength and Deformation Mechanism in a Single Crystal CoNi-base Superalloy

Effects of Co content on tensile properties and deformation behaviors of Ni-based disk superalloys at different temperatures

Effect of Ti and Al on Microstructure and Partitioning Behavior of Alloying Elements in Ni-based Powder Metallurgy Superalloys

Tensile Properties and Deformation Mechanisms of Ni–Co–W Based Superalloy with High γ′ Content

L1 2 nanoparticle-strengthened CoNi-based superalloy with ultrahigh yield stress developed using CALPHAD method

Effect of W Addition on the Solidification Microstructure and Element Distribution Behavior in Ti-42Al-5Mn Alloy