Abstract:After long-term service, metallic pipe components in nuclear power plant, chemical, petroleum industries will experience wear, leading to wall thinning. Severe thinning would affect the structural integrity, and thus a capability was required to assess the thinned components. The greatest weakening was normally near pressurized cylinder and nozzle intersection. In this study, the finite element method was used to determine the remaining structural capacity of lateral nozzles which had been subjected to local wall thinning. The study was divided into two main parts; a stress analysis at the lateral nozzles and piping having wall thinning, and a fatigue analysis of damaged intersections subject to cyclical loading. A finite element analysis (FEA) was carried out for the cylinder-nozzle intersections, to determine the stress concentration factor (SCF). 3D elements were used for the lateral nozzles. An evaluation was made of the effect on the SCF and fatigue damage coefficient of the growth of the thinning away from the intersection. Finally, a parametric study was conducted in which the SCF was computed for a number of intersections, initially considered undamaged, and then with wall thinning damage. Charts based on the results are provided for the convenience of engineers. A preliminary fatigue analysis was carried out to compare the performance under internal pressure of cylinder-nozzle intersections, without and with wall thinning damage. According to orthogonal design method, orthogonal table L9(3(4)) was established in order to analyze the SCF and fatigue damage coefficient of lateral nozzle with local wall thinning. Dimensionless relation of SCF, fatigue damage coefficient and defect length, defect depth, defect width and the angle of the cylinder and nozzle was obtained based on multiple regression method, respectively.

LES study on the turbulent thermal stratification and thermo-mechanical fatigue analysis for NPP surge line

Numerical Investigation on the Thermal Stratification in a Pressurizer Surge Line

Numerical Study on the Thermal Stratification Characteristics of AP1000 Pressurizer Surge Line

Experimental Investigation on Thermal Stratification in A Pressurizer Surge Line with Different Arrangements

Experimental Investigation of Thermal Stratification in a Pressurizer Surge Line

Transient Behaviors of Thermo-Hydraulic and Thermal Stratification in the Pressurizer Surgeline for the Nuclear Power Plant

Numerical Study on the Turbulence Penetration and Thermal Stratification Characteristics of CFETR Divertor PHTS Pressurizer Surge Line

Analysis of Effect of Pipe Type on Surge Line Thermal Stratification

Experimental Investigation on Heat Transfer Characteristics in a Safety Injection Nozzle Component in PWR

Experimental Investigation of Entrainment Effect on the Countercurrent Flow in the Hot Leg and Pressurizer Surge Line Assembly of Third-Generation Passive Nuclear Reactors

Study of Jet Characteristics and Structural Fatigue in the Upper Chamber of a Lead-Bismuth Eutectic Cooled Reactor Based on Fluid-Structure Coupling Methods

Numerical Study on the Thermal Stratification Characteristics in the Upper Plenum of Sodium-Cooled Fast Reactor (SFR)

Thermal fatigue analysis of structures subjected to liquid metal jets at different temperatures in the Gen-IV nuclear energy system

Multiscale Thermal Hydraulic Study under the Inadvertent Safety Injection System Operation Scenario of Typical Pressurized Water Reactor

Investigation on thermal stratification and turbulent penetration in a pressurizer surge line with an overall out-surge flow

Thermal Hydraulic and Stress Coupling Analysis for AP1000 Pressurized Thermal Shock (PTS) Study under SBLOCA Scenario

Validation of a Methodology for Thermal Stratification Analysis in Sodium-Cooled Fast Reactors

Fatigue and Fracture Analysis on EAST Divertor Monoblock Heat Sink in H-mode Operation

Analysis of the Effect of Thermal Stratification on the Natural Circulation Decay Heat Removal of Sodium-Cooled Fast Reactor

Numerical simulation on the thermal stratification in the lead pool of lead-cooled fast reactor (LFR)

Stress Concentration Factor and Fatigue Analysis of a Lateral Nozzle with Local Wall Thinning