Abstract:A series of poly (arylene ether sulfone)s with high molecular weight was prepared from 4-fluorophenyl sulfone, 4, 4'-biphenol and bis (4-hydroxyphenyl) sulfone with different mole ratio. Due to the large difference between the electronic effects of biphenyl fragment and phenyl sulfone fragment on the polymer, the sulfonation reaction is easily carried out on biphenyl fragments with higher electron cloud density. The sulfonic acid groups were introduced to ortho-position of the oxy ether group on the biphenyl and sulfonation degree were successfully predicted after post-sulfonation process. Sulfonated polylarylene ether sulfone (SPAES) based proton exchange membranes (PEM) were prepared by solution casting method , of which relative viscosity , ion exchange capacity (IEC) , water uptake and swell ratio , proton conductivity , oxidative stability , mechanical properties and cell performance were investigated. Relative viscosity of sulfonated copolymers was higher than 1. 2 dL/g. The sulfonated copolymers showed that titration and 'H nuclear magnetic resonance calculated value of IEC were accordingly to that of theoretical. Water uptake and swell ratio obviously increased with increasing of IEC and temperature, and the size change ratio of the thickness direction was larger than that of plane direction in the membranes. The thermal gravimetric analyse (TGA) results indicated that the PEMs have the decompose temperature at about 280 degrees C . All the PEMs showed maximum tensile strength above 50 MPa, and the elongation at break over 15% at 20 degrees C and 20% RH. Free radical oxidative stability test showed the PEMs with low IEC become brittle in Fenton' s reagent over 200 h at 20 degrees C. The proton conductivity of PEMs were increased rapidly with the increase of the IEC and temperature, for example, the conductivity of M2-SPAES(1.34 mmol/g) and M4-SPAES(1.60 mmol/g) were 68 and 89 mS/ cm at 60 degrees C in water, and 99 and 129 mS/cm at 80 degrees C in water, respectively. H-2/O-2 Fuel cell performance showed that the open circuit voltage and maximum power output were higher than 1.0 V and 0.54 W/cm(2) under 60 degrees C , 80% RH and 0.1 MPa back pressure, respectively.

Properties of Multiblock Sulfonated Poly(arylene Ether Sulfone)s Synthesized by Precise Controllable Post-sulfonation for Proton Exchange Membranes

Sulfonated Polyaryletherketone with Pendant Benzimidazole Groups for Proton Exchange Membranes

PEMs with High Proton Conductivity and Excellent Methanol Resistance Based on Sulfonated Poly (aryl Ether Ketone Sulfone) Containing Comb-Shaped Structures for DMFCs Applications

Precise Controllable Post-sulfonation for Preparation of Sulfonated Poly (arylene ether sulfone)s and Their Properties for Proton Exchange Membrane

Synthesis and Properties of Novel Side‐Chain Sulfonated Poly(Arylene Ether Sulfone)s for Proton Exchange Membranes

Sulfonated Polymers Containing Polyhedral Oligomeric Silsesquioxane (poss) Core for High Performance Proton Exchange Membranes

Synthesis and Properties of Proton Exchange Membranes Based on Cross-linked Block Sulfonated Poly(arylene Ether Sulfone)s

Preparation of Blocked Sulfonated Polyaryle Ether Sulfone and Its Proton Exchange Membrane Properties

Multiblock sulfonated poly(arylene ether sulfone)s with fluorenyl hydrophilic moieties for PEMFC applications

Concentrated sulfonated poly (ether sulfone)s as proton exchange membranes

A Novel Synthesis Approach to Partially Fluorinated Sulfonimide Based Poly (arylene Ether Sulfone) S for Proton Exchange Membrane

Preparation and Characterization of Sulfonated Poly(Arylene Ether Ketone) Copolymers with Pendant Sulfoalkyl Groups As Proton Exchange Membranes

Morphological Investigations of Block Sulfonated Poly(Arylene Ether Ketone) Copolymers As Potential Proton Exchange Membranes

A Novel Approach to Prepare Photocrosslinked Sulfonated Poly(arylene Ether Sulfone) for Proton Exchange Membrane

Spectroscopy Analysis of Sulfonated Poly (arylene Ether Ketone Sulfone) on Side Chain for Proton Exchange Membrane

Poly(Arylene Ether)s with Sulfonic Acid Groups on the Backbone and Pendant for Proton Exchange Membranes Used in PEMFC Applications

Poly(arylene Ether)s with Pendant Sulfoalkoxy Groups Prepared by Direct Copolymerization Method for Proton Exchange Membranes

Synthesis Of Copoly(Aryl Ether Ether Nitrile)S Containing Sulfonic Acid Groups For Pem Application

DIRECT SYNTHESIS AND PROPRTIES OF SULFONATED POLY(ARYLENE ETHER SULFONE) COPOLYMERS FOR PROTON EXCHANGE MEMBRANES IN FUELCELLS

Synthesis and Properties of Sulfonated Poly(arylene Ether Phosphine Oxide)s for Proton Exchange Membranes

Synthesis and Characterization of Novel Sulfonated Poly(Arylene Ether Ketone) Copolymers with Pendant Carboxylic Acid Groups for Proton Exchange Membranes