Synthesis and Characterization of Sulfonated Poly(aryl Ether Sulfone) Containing Pendent Quaternary Ammonium Groups for Proton Exchange Membranes
Qiang Zhang,Qifeng Zhang,Suobo Zhang,Shenghai Li
DOI: https://doi.org/10.1016/j.memsci.2010.02.068
IF: 9.5
2010-01-01
Journal of Membrane Science
Abstract:A new biphenol monomer, 2-(2-(dimethylamino)ethyl)-3,3′-bis(4-hydroxyphenyl)isoindolin-1-one (CPPH), was easily prepared by the reaction of phenolphthalein with N,N-dimethylethane-1,2-diamine. Novel polyampholyte, sulfonated poly(aryl ether sulfone)s with pendent alkyl ammonium groups PESQ-x-y, were prepared by copolymerization of CPPH, 4,4′-biphenol, 3,3′-disulfonated-4,4′-dichlorodiphenyl sulfone, and 4,4′-dichlorodiphenyl sulfone, and this was followed by reaction with iodomethane. PESQ-x-y was able to form uniform and tough membranes by simple solution casting. Moreover, the material exhibited a low water uptake as well as a decent dimensional stability in water, even at high temperature (e.g. 100°C), as a result of the strong electrostatic interactions between the alkyl ammonium and sulfonic acid groups. The PESQ-10-50 copolymer membrane with an ion-exchange capacity (IEC) of 1.65mequiv./g, displayed a lower water uptake (58.9%), but a higher proton conductivity (0.082S/cm) than a PES-40 membrane without alkyl ammonium groups (IEC=1.67mequiv./g, WU=85.4%, σ=0.069S/cm) at 20°C.