Microstructure and Mechanical Properties of Al–Mg-Sc-Zr Welded Joint

Wen S. H.,Jiao H. J.,Zhou L. G.,Zhang Q. S.,Wu S. J.

DOI: https://doi.org/10.1007/s40194-022-01313-5

IF: 2.1

2022-01-01

Welding in the World

Abstract:The Al–Mg-Sc-Zr alloy was welded using three kinds of weld filler wires containing different additions of zirconium, scandium, titanium, and boron. With a uniform Al3(Sc,Zr) and TiB2 dispersed on the α-Al matrix in the fusion zone, the Al–Mg-Sc-Zr-TiB2 weld displayed the best tensile property, its yield strength and tensile strength of welded joint with reinforcement reached 232.2 MPa and 386.3 MPa, and the yield strength and tensile strength of weld without reinforcement was about 208.0 MPa and 358.4 MPa, respectively. The fractions of the Al3(Sc,Zr) phase in the fusion zone was relative to the Sc and Zr content. A remarkable grain refining effect was observed for addition of Zr, Sc, and TiB2, because the formation of Al3(Sc,Zr) and TiB2 can act as nucleant particles during solidification. With the increase of Sc/Zr and TiB2 addition in the melting fusion, the tensile strength, yield strength, and corresponding elongation of the 2195 Al-Li alloy increase, while the impact toughness slightly decreases.