Comparison of Microstructure and Mechanical Properties of TIG and Laser Welding Joints of a New Al–Zn–Mg–Cu Alloy

Zhang Liang,Li Xiaoyan,Nie Zuoren,Huang Hui,Sun Jiantong,Sun Zhongguo

DOI: https://doi.org/10.1016/j.matdes.2015.12.117

2016-01-01

Abstract:New Al-Zn-Mg-Cu alloy sheets have been welded using automatic TIG welding with filler wires. The microstructure characteristics and mechanical properties of weld joints were analyzed. Results show that the fusion zone (FZ) is comprised of a non-dendritic equiaxed grain zone (EQZ) and a coarser dendritic equiaxed grains, and the fusion boundary does not nucleate epitaxially from the heat affected zone (HAZ) substrate, and the compound T (AlZnMgCu) phase precipitates discretely on grain boundaries. The HAZ is divided into a solid solution zone that is close to the FZ and an overaging zone which is farther away from the FZ because of an alteration of the strengthening precipitates, resulting in different microhardness values, and the grains in the HAZ are elongated as same as the base metal (BM) and they do not become coarser compared with the BM. The minimum microhardness of the joint is obtained in the FZ and the value is approximately HV 1200 MPa, and that of the BM is about HV 1840 MPa, and the ultimate tensile strength of joints is 421.75 MPa which is 65.08% of that of the BM. Samples of the tensile test fracture at the FZ and the fractured surface is of ductile fracture characteristics. Small particles whose composition is almost same as the compound T phase are observed at the bottom of dimples.