Abstract:Sulfate-reducing bacteria (SRB) can regulate environmental pH because of their metabolism. Because local acidification results in pitting corrosion, the potential capacity of pH regulation by SRB would have important consequences for electrochemical aspects of the bio-corrosion process. This study focused on identifying the effect of pH on the corrosion of duplex stainless steel 2205 in a nutrient-rich artificial seawater medium containing SRB species, Desulfovibrio vulgaris . Duplex stainless steel samples were exposed to the medium for 13 days at 37°C at pH ranging from 4.0 to 7.4. The open-circuit potential value, sulfide level, pH and number of bacteria in the medium were recorded daily. Electrochemical impedance spectroscopy (EIS) and potentiodynamic polarization were used to study the properties of the biofilms at the end of the experiments and the corrosion behaviour of the material. Inductively coupled plasma mass spectrometry was used to measure the concentration of cations Fe, Ni, Mo, Mn, Cr in the experimental solution after 13 days. Scanning electron microscopy and energy-dispersive X-ray spectroscopy (EDX) were used for surface analysis. The results showed the pH changed from acidic values set at the beginning of the experiment to approximately pH 7.5 after 5 days owing to bacterial metabolism. After 13 days, the highest iron concentration was in the solution that was initially at pH 4 accompanied by pitting on the stainless steel. Sulfur was present on all specimens but with more sulfur at pH 4 in the EDX spectra. EIS showed the film resistance of the specimen at pH 4 was much lower than at pH 7.4 which suggests the corrosion resistance of the stainless steel was better at higher pH. The results of this study suggest that the corrosion process for the first few days exposure at low pH was driven by pH in solution rather than by bacteria. The increasing pH during the course of the experiment slowed down the corrosion process of materials originally at low pH. The nature and mechanism of SRB attack on duplex stainless steel at different acidic environments are discussed.

Effects of Cathodic Polarization on X65 Steel Inhibition Behavior and Mechanism of Mixed Microorganisms Induced Corrosion in Seawater

Some data on two purified kininogens from human plasma.

Effect of anodic polarization treatment on microbiologically influenced corrosion resistance of Cu-bearing stainless steel against marine Pseudomonas aeruginosa

Effects of cathodic protection potential on microbiologically induced corrosion behavior of X70 steel in a near-neutral pH solution

Influence of temperature on the cathodic polarization behavior and calcareous deposit properties of X65 steel in sea water

Electrochemical investigation of the "double-edged" effect of low-dose biocide and exogenous electron shuttle on microbial corrosion behavior of carbon steel and copper in enriched seawater

Corrosion inhibition study of marine Streptomyces against sulfate-reducing bacteria in oilfield produced water

Corrosion Behavior of X70 Pipeline Steel in 3.5% Nacl Solution under the Synergistic Action of Cathodic Protection and Sulfate- reducing Bacteria

Influence of anion and sulfate-reducing bacteria on the stress corrosion behavior and mechanism of X70 steel in a marine mud environment

Influence of calcareous deposit on corrosion behavior of Q235 carbon steel with sulfate-reducing bacteria

Effect of One Sulfate-Reducing Bacterium SRB-Z Isolated from Pearl River on the Corrosion Behavior of Q235 Carbon Steel

Effects Of Sulfate-Reducing Bacteria on Corrosion of Carbon Steel Q235 in the Crevice by EIS

Study on the screening of marine beneficial bacteria and the inhibition of sulfate-reducing bacteria corrosion in marine oil field produced water

Effect of Ochrobactrum sp. on the Corrosion Behavior of 10MnNiCrCu Steel in Simulated Marine Environment

Corrosion Behavior and Interaction of Mixed Bacteria on Carbon Steel in Reclaimed Water

Influence of aerobic bacteria on corrosion inhibition of oil bushing steel in the oilfield stratum water

Effect of pH regulation by sulfate-reducing bacteria on corrosion behaviour of duplex stainless steel 2205 in acidic artificial seawater

Specification of sulfate reducing bacteria biofilms accumulation effects on corrosion initiation

Effect of SO42− in aerobic/anaerobic environment and its interaction with HCO3− on corrosion behavior of carbon steel

A comparative study of the corrosion of Q235 carbon steel in six different strains of marine-isolated sulfate reducing prokaryote

Corrosion Behavior of Carbon Steel in the Presence of <Emphasis Type="Italic">Escherichia coli</Emphasis> and <Emphasis Type="Italic">Pseudomonas fluorescens</Emphasis> Biofilm in Reclaimed Water