Abstract:The current study highlights the corrosion consequences observed in API 5L X65 carbon steel when exposed to a marine-like environment containing carbon dioxide (CO2), in the presence of sulfate- reducing bacteria consortium (C-SRB), iron-reducing bacteria consortium (C-IRB), and a combination of both (C-SRB+C-IRB). The corrosion behaviour was assessed through the utilisation of weight loss and surface analysis techniques. The biofilms and corrosion products were characterised using field emission scanning electron microscopy (FESEM) and infinite focus microscope (IFM), respectively. The results obtained from the weight loss technique provided confirmation that in the absence of bacteria, uniform corrosion was the prevailing mechanism in the medium. The uniform corrosion rate was found to be 0.95 mm/year, which was higher than the pit penetration rate of 0.28 mm/year. The combined actions of the C-SRB+C-IRB consortium result in a synergistic impact, leading to a significantly higher rate of pit penetration compared to the individual activities of SRB. Specifically, the pit penetration rate value of 2.13 mm/year is observed, which is notably higher than the uniform corrosion rate of 0.59 mm/year. The utilisation of surface analysis techniques has shown evidence of the existence of sulfur on carbon steel samples that were subjected to exposure from the C-SRB+C-IRB consortium in a CO2 environment. This sulphur presence is believed to potentially play a role in the development of the iron sulphide (FeS) layer. FeS presence is a contributing factor to the occurrence of pit corrosion due to the SRB metabolite activities. The activities of these metabolites readily dissolve in the medium, hence altering the chemical interface properties of both the metal and the biofilm. For specimens exposed to C-SRB only, the results obtained were almost identical to exposure to the C- SRB+C-IRB consortium. However, the corrosion rate value measured for the C-SRB+C-IRB consortium was higher due to the synergistic effect of the two bacteria. In conclusion, the presence of C-SRB alone and the consortium of C-SRB+C-IRB in a CO2 environment induces the formation of pitting corrosion. The findings of this study are presumed to contribute a deep understanding of the microbiology-influenced corrosion (MIC) mechanism in CO2 environments troubling the oil and gas industry. With a better understanding of MIC, new and improved corrosion prevention strategies can be put into action.

Corrosion inhibition study of marine Streptomyces against sulfate-reducing bacteria in oilfield produced water

Study on the screening of marine beneficial bacteria and the inhibition of sulfate-reducing bacteria corrosion in marine oil field produced water

Corrosion behavior of X65 steel in seawater containing sulfate reducing bacteria under aerobic conditions

Metagenomics diversity analysis of sulfate-reducing bacteria and their impact on biocorrosion and mitigation approach using an organometallic inhibitor

Influence of anion and sulfate-reducing bacteria on the stress corrosion behavior and mechanism of X70 steel in a marine mud environment

Effect of One Sulfate-Reducing Bacterium SRB-Z Isolated from Pearl River on the Corrosion Behavior of Q235 Carbon Steel

Specification of sulfate reducing bacteria biofilms accumulation effects on corrosion initiation

Corrosion inhibition of deposit-covered X80 pipeline steel in seawater containing Pseudomonas stutzeri.

Influence of aerobic bacteria on corrosion inhibition of oil bushing steel in the oilfield stratum water

Synergistic Effect between Chloride and Sulfate Reducing Bacteria in Corrosion Inhibition of X100 Pipeline Steel in Marine Environment

Effects Of Sulfate-Reducing Bacteria on Corrosion of Carbon Steel Q235 in the Crevice by EIS

Influence of Sulfate and Iron Reducing Bacteria on Carbon Steel Corrosion in Marine Environments

A comparative study of the corrosion of Q235 carbon steel in six different strains of marine-isolated sulfate reducing prokaryote

Corrosion Behavior on 20# Pipeline Steel by Sulfate-Reducing Bacteria in Simulated NaCl Alkali/Surfactant/Polymer Produced Solution

Effect of nutrient concentration on corrosion mechanism of X80 pipeline steel caused by sulfate-reducing bacteria

Insight into sulfate-reducing bacteria corrosion behavior of X80 pipeline steel welded joint in a soil solution

Influence of calcareous deposit on corrosion behavior of Q235 carbon steel with sulfate-reducing bacteria

Corrosion of Q235 carbon steel induced by sulfate-reducing bacteria in groundwater: corrosion behavior, corrosion product, and microbial community structure

Effect of salt-resistant polymer flooding system SRB on corrosion behavior of 20# carbon steel under deposition

Effect of pH regulation by sulfate-reducing bacteria on corrosion behaviour of duplex stainless steel 2205 in acidic artificial seawater

Accelerated corrosion of pipeline steel in the presence of Desulfovibrio desulfuricans biofilm due to carbon source deprivation in CO2 saturated medium