Abstract:The current study highlights the corrosion consequences observed in API 5L X65 carbon steel when exposed to a marine-like environment containing carbon dioxide (CO2), in the presence of sulfate- reducing bacteria consortium (C-SRB), iron-reducing bacteria consortium (C-IRB), and a combination of both (C-SRB+C-IRB). The corrosion behaviour was assessed through the utilisation of weight loss and surface analysis techniques. The biofilms and corrosion products were characterised using field emission scanning electron microscopy (FESEM) and infinite focus microscope (IFM), respectively. The results obtained from the weight loss technique provided confirmation that in the absence of bacteria, uniform corrosion was the prevailing mechanism in the medium. The uniform corrosion rate was found to be 0.95 mm/year, which was higher than the pit penetration rate of 0.28 mm/year. The combined actions of the C-SRB+C-IRB consortium result in a synergistic impact, leading to a significantly higher rate of pit penetration compared to the individual activities of SRB. Specifically, the pit penetration rate value of 2.13 mm/year is observed, which is notably higher than the uniform corrosion rate of 0.59 mm/year. The utilisation of surface analysis techniques has shown evidence of the existence of sulfur on carbon steel samples that were subjected to exposure from the C-SRB+C-IRB consortium in a CO2 environment. This sulphur presence is believed to potentially play a role in the development of the iron sulphide (FeS) layer. FeS presence is a contributing factor to the occurrence of pit corrosion due to the SRB metabolite activities. The activities of these metabolites readily dissolve in the medium, hence altering the chemical interface properties of both the metal and the biofilm. For specimens exposed to C-SRB only, the results obtained were almost identical to exposure to the C- SRB+C-IRB consortium. However, the corrosion rate value measured for the C-SRB+C-IRB consortium was higher due to the synergistic effect of the two bacteria. In conclusion, the presence of C-SRB alone and the consortium of C-SRB+C-IRB in a CO2 environment induces the formation of pitting corrosion. The findings of this study are presumed to contribute a deep understanding of the microbiology-influenced corrosion (MIC) mechanism in CO2 environments troubling the oil and gas industry. With a better understanding of MIC, new and improved corrosion prevention strategies can be put into action.

Influence of aerobic bacteria on corrosion inhibition of oil bushing steel in the oilfield stratum water

Influence of microbial community on iron release under stagnation condition in drinking water systems

Study on the screening of marine beneficial bacteria and the inhibition of sulfate-reducing bacteria corrosion in marine oil field produced water

Corrosion inhibition study of marine Streptomyces against sulfate-reducing bacteria in oilfield produced water

Corrosion behavior of X65 steel in seawater containing sulfate reducing bacteria under aerobic conditions

Corrosion inhibition of deposit-covered X80 pipeline steel in seawater containing Pseudomonas stutzeri.

Influence of Sulfate and Iron Reducing Bacteria on Carbon Steel Corrosion in Marine Environments

Synergistic effect on corrosion behavior of X80 steel influenced by Pseudomonas aeruginosa and Acetobacter aceti

A comparative study of the corrosion of Q235 carbon steel in six different strains of marine-isolated sulfate reducing prokaryote

Effect of Ochrobactrum sp. on the Corrosion Behavior of 10MnNiCrCu Steel in Simulated Marine Environment

Corrosion Behavior and Interaction of Mixed Bacteria on Carbon Steel in Reclaimed Water

Responses of Microbial Community Composition to Temperature Gradient and Carbon Steel Corrosion in Production Water of Petroleum Reservoir

Inhibition of Carbon Steel Corrosion Behavior by Extracellular Polymeric Substances of Lactobacillus Reuteri

Corrosion Behavior of Carbon Steel in the Presence of <Emphasis Type="Italic">Escherichia coli</Emphasis> and <Emphasis Type="Italic">Pseudomonas fluorescens</Emphasis> Biofilm in Reclaimed Water

Corrosion Behavior of AISI 1045 Steel in Seawater in the Presence of Flavobacterium sp.

A study on the microbial biocorrosion behavior of API 5 L X65 carbon steel exposed to seawater

Experimental Investigation on Corrosion Behavior of X80 Pipeline Steel under Carbon Dioxide Aqueous Conditions

Influence of anion and sulfate-reducing bacteria on the stress corrosion behavior and mechanism of X70 steel in a marine mud environment

Effect of Pseudomonas aeruginosa on Corrosion Behavior of X65 Carbon Steel

Microbiologically influenced corrosion of steel in coastal surface seawater contaminated by crude oil

Effect of Bacterial Communities on the Formation of Cast Iron Corrosion Tubercles in Reclaimed Water