Abstract:Producing biodegradable plastics from CO2 is a promising methodology for recycling industrial waste gas, and the conservation of environment and energy. Propylene oxide (PO) has been commonly used to copolymerize with CO2 to yield biodegradable poly(propylene carbonate) (PPC). PPC exhibits excellent transparency, low water and oxygen permeability as well as high flexibility. But low glass transition temperature (T-g) limited its practical applications. In recent years, the copolymerization of PO, CO2 with phthalic anhydride (PA) provides a robust and economical method to improve PPC's thermal and mechanical performance. In this study, to explore the relationship between the sequence structure and the properties of CO2/PO/PA terpolymer (PPC-P), PPC-P terpolymers with similar polyester (PE) content and molecular weight but different sequence structures (block, tapered and random) were synthesized through one-pot two-step method or one-pot one-step method using non-metallic catalytic system (TEB/PPNCI). The effects of polymerization temperature and reaction time on the composition and molecular weight of the PPC-P were systematically studied, and the PE content and molecular weight of all the terpolymers were controlled to be around 45% and 5.0x 10(4), respectively for comparison. The typical sequence structure characteristics of the terpolymers were proven by H-1-NMR. Differential scanning calorimetry (DSC), thermogravimetric analysis (TGA) and tensile test were used to characterize the thermal and mechanical properties of the PPC-P terpolymers. The block terpolymer shows two glass-transition temperature (T-g) (43 and 54 degrees C), while the tapered and random terpolymer has only one T-g (51, 50 degrees C). The T-d5 of the block terpolymer (263 degrees C) is lower than that of the tapered and random terpolymer (around 273 degrees C), indicating the poorer thermostability of block terpolymer. The three terpolymers with different sequence structures have similar tensile strength (around 35 MPa), all belonging to hard and brittle materials. [GRAPHICS] .

Study of the Synthesis of CO<sub>2</sub>/Propylene Epoxide/Phthalic Anhydride Terpolymers with Different Sequence Structures and Their Properties