Comparative Studies of Polycrystal and Single-Crystal LiNi 0.6 Co 0.2 Mn 0.2 O 2 in Terms of Physical and Electrochemical Performance
Guangxin Li,Ya Wen,BinBin Chu,Longzhen You,Lingfeng Xue,Xiang Chen,Tao Huang,Aishui Yu
DOI: https://doi.org/10.1021/acssuschemeng.1c03002
2021-08-27
Abstract:Herein, the physical properties (structure, morphology, lattice strain, specific surface area, particle size, and compaction density) of polycrystal LiNi0.6Co0.2Mn0.2O2 (PC622) and single-crystal LiNi0.6Co0.2Mn0.2O2 (SC622) materials have been comparatively investigated. We have also investigated the electrochemical performance of PC622 and SC622 electrodes with different compaction densities. The results show that secondary particle collapse is widely observed in highly compacted PC622 electrodes. Moreover, the improvement in compaction density is beneficial for specific capacity and initial Coulombic efficiency. SC622 exhibits good cycling performance at room temperature (25 °C) and an elevated temperature (55 °C) even when the density increases to 3.52 g cm–3. The capacity retention values of SC622 are 86.0% (150 cycles, 1C, 25 °C) and 94.1% (100 cycles, 1C, 55 °C), which are significantly higher than PC622 (78.7 and 75.7%, respectively). Further studies via TEM on these electrodes with high compaction densities show that a thinner rock-salt phase region is found on the surface of the SC622 particles. Hence, SC622 maintains crystallite integration, excellent cycling performance, and thermal stability and can easily be manufactured into high compaction density electrodes.The Supporting Information is available free of charge at https://pubs.acs.org/doi/10.1021/acssuschemeng.1c03002.ICP of the precursors, PC622, and SC622; Rietveld refinements of the PC622 and SC622; SEM of precursors; EDS mapping of Ni, Co, Mn, and O in the PC622 sample; cycling performance and detailed electrochemical performance of PC622 and SC622 with different compacted densities; GITT and GITT curves for PC622 and SC622 with a compacted density of 3.52 g cm–3; and ex-XRD patterns of the PC622 and SC622 before and after cycling (PDF)This article has not yet been cited by other publications.
chemistry, multidisciplinary,engineering, chemical,green & sustainable science & technology