Abstract:TC4 titanium alloy wire arc additive manufacturing (WAAM) is easy to produce coarse columnar β grain structure which affects mechanical properties. So in this paper, an innovative process of interpass milling assisted TC4 titanium alloy gas tungsten arc welding (GTAW) WAAM is proposed. The controlling interpass milling depth is used to improve the microstructure and mechanical properties of TC4 titanium alloy parts during the GTAW-WAAM. The results showed that the coarse columnar β grains and fine α phase were observed in the non-interpass milling part. When the interpass milling assistance GTAW-WAAM was employed, the coarse columnar β grains transformed into short columnar and equiaxed grains. With the increased of interpass milling depth, the average size of α phase was gradually refined to 13.5 μm below. The highest average microhardness in the top, middle and bottom areas obtained by using the interpass milling depth of 300 μm were 369 HV 0.2 , 371 HV 0.2 and 371 HV 0.2 respectively, which was increased by 32 HV 0.2 , 28 HV 0.2 and 26 HV 0.2 compared with non-interpass milling respectively. The horizontal and vertical ultimate tensile strength first increases and then decreases with the increase of interpass milling depth, reaching its maximum at a milling depth of 300 μm. The highest tensile strength of the horizontal and vertical directions obtained by using the interpass milling depth of 300 μm were 1022 MPa and 1042 MPa. The level of the ultimate tensile strength is related to the combined proportion of total average β grain size and total average <15 μm α phase size, and the proportion of both is balanced and maximized to obtain the maximum ultimate tensile strength. The interpass milling depth of 300 μm satisfies both conditions, so its maximum horizontal and vertical ultimate tensile strength is achieved. Fracture type of tensile specimen was ductile fracture due to observing a lot of dimples on the fracture morphology. The above conclusions show that interpass milling is an aided process to effectively improve the microstructure and mechanical properties of TC4 titanium alloy GTAW wire arc additive manufacturing thin-walled parts, which has high research significance and practical value.

Towards Superior Fatigue Crack Growth Resistance of TC4-DT Alloy by In-Situ Rolled Wire-Arc Additive Manufacturing

Isotropy of Fatigue Crack Growth in Hybrid Additive Manufactured Ti6Al4V ELI Titanium Alloy

Effect of Fast Frequency Double Pulse Current on Microstructural Characteristics and Mechanical Properties of Wire Arc Additively Manufactured Ti-6Al-4V Alloy

Predicting the Effect of Surface Waviness on Fatigue Life of a Wire + Arc Additive Manufactured Ti-6Al-4V Alloy

Fatigue and anisotropic behavior of wire-arc additive manufactured TC17 titanium alloy

Defect-correlated fatigue resistance of additively manufactured Al-Mg4.5Mn alloy with in situ micro-rolling

Improvement of Microstructure and Mechanical Properties of TC4 Titanium Alloy GTAW based Wire Arc Additive Manufacturing by using Interpass Milling

Enhanced strength of additively manufactured Ti-6Al-4V alloy through multistage strain hardening

Hot Deformation Behavior and Process Optimization of TC4-DT Alloy Fabricated by Wire and Arc Additive Manufacturing with In-Situ Forging

Fatigue Crack Initiation and Growth Behaviors of Additively Manufactured Ti-6AI-4V Alloy After Hot Isostatic Pressing Post-Process

Fatigue crack growth behaviour of wire arc additively manufactured steels

Microstructural Causes and Mechanisms of Crack Growth Rate Transition and Fluctuation of Additively Manufactured Titanium Alloy

Effect of microstructure on short fatigue crack growth of wire arc additive manufactured Ti-6Al-4V

Precipitation Phenomena and Strengthening Mechanism of Al–Cu Alloys Deposited by In-Situ Rolled Wire-Arc Additive Manufacturing

Fatigue of Wire+arc Additive Manufactured Ti-6Al-4V in Presence of Process-Induced Porosity Defects

Anisotropy of Fatigue Crack Growth in Wire Arc Additive Manufactured Ti-6Al-4V

Investigation of High-Cycle Fatigue Properties of Wire Arc Additive Manufacturing 13cr4ni Martensitic Stainless Steel

Microstructure and Fatigue Properties of Ti-48Al Alloy Fabricated by the Twin-Wire Plasma Arc Additive Manufacturing

Fabrication of γ-TiAl intermetallic alloy using the twin-wire plasma arc additive manufacturing process: Microstructure evolution and mechanical properties

A comparison on microstructure features, compression property and wear performance of TC4 and TC11 alloys fabricated by multi-wire arc additive manufacturing

Fatigue Crack Growth Rates and Crack Tip Opening Loads in CT Specimens Made of SDSS and Manufactured Using WAAM