Abstract:In this study, the effect of dual-pulsed gas metal arc welding (DP-GMAW) parameters such as thermal frequency and current amplitude on weldability, microstructural evolution, and mechanical properties of AA7075 alloy joint was investigated. ER53356 filler metal was employed to make AA7075 alloy joints. Thermal frequency in three levels of 1, 2, and 3 Hz was used during the welding process. And current amplitudes of 9, 27, and 45 A were used in three levels as well. After the DP-GMAW process, the welded samples were first checked visually, by a liquid penetrant method, to make sure of their welding soundness. No surface defect or crack was observed. An optical microscope (OM) and a scanning electron microscope (SEM) equipped with energy-dispersive spectroscopy (EDS) were used for microstructural analyses. The hardness of the base metal (BM) and different areas of the welded parts was measured by a microhardness testing method. Results showed that no visual defects were visible on the surface of the joints made under different PD-GMAW variables. As well, microstructural analyses showed that increasing the thermal frequency and current amplitude not only reduced the grain size of the weld metal (WM) and the heat-affected zone (HAZ) but also increased the hardness of these regions. The most refined structure was obtained by employing 2 Hz as frequency and 45 A as current amplitude. The average grain size under these conditions was 71 μm and 52 μm, respectively. It was also observed that increasing the current amplitude had the highest impact in reducing the grain size of the WM. The hardness of the WM and the HAZ, under the optimum frequency, was 91 HVN and 153 HVN, respectively. These values were 85 HVN and 38 HVN under the optimum current amplitude. Moreover, hardness was increased in the HAZ compared with the base metal in all welding conditions. Increasing the thermal frequency not only decreased the distance between the ripples but also increased the number of peak waves created in the fusion line. This was particularly the case in the longitudinal section of the weld and reduced the distance between these waves. On the other hand, increasing the frequency and current amplitude has led to the reduction of porosity in the WM. Finally, increasing the frequency from 1 to 3 Hz led to a 33% reduction in the porosity of the WM. This is while 66% reduction of porosity in the WM was obtained by increasing the current amplitude from 9 to 45 A.

Effect of Low Heat-Input Double-Pulse Gas Metal Arc Welding on Weld Formation and Microstructure of 6061 Aluminium Alloy

Heat input characteristics and weld bead formation in double-wire double-pulsed GMAW of aluminum alloy under different low-frequency phases

Process Optimization, Microstructure and Mechanical Properties of Wire Arc Additive Manufacturing of Aluminum Alloy by Using DP-GMAW Based on Response Surface Method

Investigation on the Dynamic Behavior of Weld Pool and Weld Microstructure During DP-GMAW for Austenitic Stainless Steel

The effect of thermal frequency and current amplitude on weldability, microstructural evolution and mechanical properties of AA7075 alloy joint in DP-GMAW process

Double-Pulse Triple-Wire MIG Welding of 6082-T6 Aluminum Alloy: Process Characteristics and Joint Performances

Effect of high-frequency phase shift on metal transfer and weld formation in aluminum alloy double-wire DP-GMAW

Inhomogeneous microstructure distribution and its formation mechanism in deep penetration laser welding of medium-thick aluminum-lithium alloy plates

Refined weld microstructure and enhanced joint mechanical property of 1460 Al-Li alloys via double-pulsed variable polarity TIG arc welding

Effect of Heat Input on the Microstructure and Mechanical Properties of 6060 Aluminum Alloy/Galvanized STEEL MIG Welding–Brazing Joints

Effect of CMT Welding Heat Input on Microstructure and Properties of 2A14 Aluminum Alloy Joint

Study on the thermo-effect of P-GMAW characterized by structure-borne acoustic emission signals detected in welding on aluminum alloy

Weldability improvement by wobbling technique in high power density laser welding of two aluminum alloys: Al-5052 and Al-6061

Effect of Current on Mechanical Properties and Microstructure of Aluminum 6061 with Gas Tungsten Arc Welding Process

Effects of laser oscillating frequency on energy distribution, molten pool morphology and grain structure of AA6061/AA5182 aluminum alloys lap welding

Research on Process Characteristics and Properties in Deep-Penetration Variable-Polarity Tungsten Inert Gas Welding of AA7075 Aluminum Alloy

A novel optimizing Pulsed Plasma Gas Variable Polarity Plasma Arc Welding (PPG-VPPAW) method for improving weld quality

Influence of Metal Transfer Modes on Pore Formation during the Welding Process of AA6082/A360 Dissimilar Aluminum Alloys

Study on Morphology, Microstructure and Properties of 6063-T6 Aluminum Alloy Joints in MIG Welding

Dynamic Metal Transfer Behavior in Double-Wire DP-GMAW of Aluminum Alloy Under Different Pulse Phases

Effect of Current on the Microstructural and Mechanical Properties of Mig Welded Aa6061 Aluminum Alloy