Abstract:This study presents the alloy development of a new class of L1 2 -strengthened Co-Al-Nb-based alloys with high gamma ' -solvus temperatures together with superb strengths at both ambient and elevated temperatures. The L1 2 -Co 3 (Al, Nb) phase was found to be in equilibrium with the gamma -Co matrix and the B2-CoAl phase in the ternary Co-10Al-3Nb alloy after an isothermal aging at 700 degrees C; however, it transformed into the Laves phase as the aging temperature increased to 800 degrees C. Alloying additions of Ni helped to suppress the B2 phase formation, resulting in a clean gamma - gamma ' dual-phase microstructure. Ti and Ta elements further stabilized the L1 2 structure and increased the gamma ' -solvus temperature to 1150 degrees C without inducing the formation of any other deleterious intermetallic phases. The newly developed Co-Al-Nb-Ni-Ti-Ta multicomponent Co-rich alloy has demonstrated outstanding yield strengths at both ambient and elevated temperatures, reaching 1023 +/- 27 MPa at 25 degrees C and 897 +/- 53 MPa at 700 degrees C, respectively. Furthermore, electron microscopy analyses uncovered unique deformation substructures, in which plasticity is predominantly carried out via nanoscale matrix-channel-confined stacking faults. As determined by the first-principle calculations, the absence of particle shearing upon deformation at ambient temperature is ascribed to the ultrahigh planar fault energies of the multicomponent gamma ' precipitates. High-density superlattice-stackingfault shearing and their interactions are responsible for the yield anomaly at 700 degrees C. These findings not only provide the fundamental understanding of the deformation behavior of the L1 2 -strengthened alloys, but also demonstrate the great potential for developing next-generation high-temperature structural materials based on the multicomponent Co-rich alloy systems.

L1 2-strengthened multicomponent Co-Al-Nb-based alloys with high strength and matrix-confined stacking-fault-mediated plasticity

L12-strengthened Multicomponent Co-Al-Nb-based Alloys with High Strength and Matrix-Confined Stacking-Fault-mediated Plasticity

Microstructures and Mechanical Properties of a L12-structured Precipitation Strengthened Co-based Superalloy

L1 2 nanoparticle-strengthened CoNi-based superalloy with ultrahigh yield stress developed using CALPHAD method

L1 2 ‐Strengthened Co‐Rich Alloys for High‐Temperature Structural Applications: A Critical Review

Plastic Deformation Behaviors and Mechanical Properties of Advanced Single Crystalline CoNi-base Superalloys

Superior High-Temperature Properties and Deformation-Induced Planar Faults in a Novel L12-strengthened High-Entropy Alloy

L12 Nanoparticle-Strengthened CoNi-based Superalloy with Ultrahigh Yield Stress Developed Using CALPHAD Method

A Novel Coherent Particles-Reinforced FCC-based High-Entropy Superalloy with Superior High-Temperature Compressive Properties

Microstructures and Mechanical Properties of a L1 2 -structured precipitation Strengthened Co-based Superalloy

Synergistic Enhancement of High Temperature Strength and Ductility with a Novel Γ/ε Dual-Phase Hetero-Nanostructure in NiCoCr-based Alloys

Novel Co-Ti-V-base Superalloys Reinforced by L12-ordered Γ′ Phase

A L12 Precipitation Strengthened Co-free Medium-Entropy Alloy with Superior High-Temperature Performance

The Temperature Dependence of High-Temperature Strength and Deformation Mechanism in a Single Crystal CoNi-base Superalloy

Ab Initio Calculations and CALPHAD Assisted Design of L1 2-Hardened CoNi-Based Superalloys Exhibiting Low Mass Density, Large Misfit and High Yield Stress

Temperature-dependent Deformation Mechanisms of Γ′ Phases in a Newly Developed NiCoCr-based Superalloy

Effect of Alloying Elements on the High-Temperature Yielding Behavior of Multicomponent γ'-L12 Alloys

Theoretical Exploration of Alloying Effects on Stabilities and Mechanical Properties of γʹ Phase in Novel Co–Al–Nb-Base Superalloys

A Novel Co-Ni-Ti-V-based Superalloy Exhibiting Low Density and High Strength

A Novel Low-Density and High-Strength Fe-Ni-base High-Entropy Superalloy with Stable Γ/γ' Coherent Microstructure at 1023 K

Nano-amorphous—crystalline Dual-Phase Design of Al80Li5Mg5Zn5Cu5 Multicomponent Alloy