Temperature-dependent microstructural evolutions and deformation mechanisms of (Ni2Co2FeCr)92Al4Nb4 high-entropy alloys
J.Y. Zhang,B. Xiao,Q. Li,B.X. Cao,J.X. Hou,S.F. Liu,J.X. Zhang,W.C. Xiao,J.H. Luan,Y.L. Zhao,C.T. Liu,T. Yang,J.Y. Zhang,B. Xiao,Q. Li,B.X. Cao,J.X. Hou,S.F. Liu,J.X. Zhang,W.C. Xiao,J.H. Luan,Y.L. Zhao,C.T. Liu,T. Yang
DOI: https://doi.org/10.1016/j.jallcom.2022.165597
IF: 6.2
2022-10-15
Journal of Alloys and Compounds
Abstract:Precipitation-strengthened high-entropy alloys (HEAs) with tailored phase structures are expected to possess excellent strength-ductility combinations for advanced structural applications. In this work, we systematically studied the microstructural evolutions and mechanical behaviors of (Ni2Co2FeCr)92Al4Nb4 HEAs at different aging temperatures (700–900 °C). It was revealed that only spherical L12 phase existed in the specimen peak-aged at 700 °C without other precipitates, while in the specimen peak-aged at 800 °C, irregular precipitation of ε phase appeared on the grain boundaries in addition to the intragranular L12 phase. In strong contrast, upon peak aging at 900 °C. the fine interleaving Widmanstätten-type ε phase with an ordered hexagonal structure (D019) became the dominated precipitate. We further revealed that the coherent L12 phase provided a more effective strengthening effect than that of the ε phase, leading to the highest yield strength of ~950 MPa in the alloy peak-aged at 700 °C. The stacking faults shearing of L12 phase and the planar dislocations shearing of ε phase were identified as the main deformation mechanisms of the specimens peak-aged at 700 and 900 °C, respectively. Interestingly, the ε phase was determined to have certain plastic deformability, enabling the 900 °C peak-aged alloy to exhibit excellent tensile ductility. These findings would provide valuable guidelines for the design of precipitation-strengthened HEAs with optimized microstructures and superior mechanical properties.
materials science, multidisciplinary,chemistry, physical,metallurgy & metallurgical engineering