Abstract:Spherical nano-MoS 2 (S-MoS 2 ) has excellent lubricating properties and potential application value in engine oil additives. Engine soot can enter the engine oil, so the tribological interaction between S-MoS 2 and diesel combustion soot (DCS) should be investigated. In this study, DCS was used to simulate engine soot. The interaction was investigated in dioctyl sebacate (DOS), and the interaction mechanism was full characterized. Results showed that S-MoS 2 and DCS had obvious antagonism effects on lubrication. The 0.5% S-MoS 2 exhibited good lubricating properties in DOS, which could reduce friction by ∼22% and wear by ∼54%. However, after 0.5% S-MoS 2 was added to the 0.5% DCS contaminated DOS, the lubrication performance was not improved and was even worse than that without S-MoS 2 . When S-MoS 2 was added for DOS lubrication, a tribofilm containing MoS 2 formed on the friction surface, but simultaneously adding 0.5% DCS resulted in the disappearance of the MoS 2 tribofilm. Moreover, under the action of friction heat, DCS and S-MoS 2 could form hard Mo x C y , thereby increasing abrasive wear. Finally, a preliminary deantagonism method was provided. After 2.0% zinc isooctyl dithiophosphate was added to the above antagonistic system, the friction coefficient did not show visible changes, but the wear recovered to a level close to that when only S-MoS 2 was added. The antiantagonism method is not very satisfactory and some more efficient methods need to be further explored.

An efficient lubrication approach to mitigate soot-induced wear: Synergistic repair effect of magnetic MoS<sub>2</sub> composites and magnetic field

Preparation and tribological behaviors of magnesium silicate hydroxide-MoS2 nanoparticles as lubricant additive

The synergistic action of Ag and MoS2 on tribological properties of Al2O3/Ag(MoS2) composite coatings

Friction and self-repairing behaviour of magnesium silicate hydroxide-MoS2 lubricant additives on gray cast iron with Cr-coated steel ball friction pairs

Controllable fabrication of magnesium silicate hydroxide reinforced MoS2 hybrid nanomaterials as effective lubricant additives in PAO

Lubrication antagonism mechanism of nano-MoS2 and soot particles in ester base oil

Nano Magnesium Silicate Hydroxide as Synergistic Lubricant Additive With Micro Carbon Sphere for Enhanced Tribological Properties

The Effect of Spherical Hybrid Silica-Molybdenum Disulphide on the Lubricating Characteristics of Castor Oil

Synergistic effects between sulfur- and phosphorus-free organic molybdenums and ZDDP as lubricating additives in PAO 6

Tribological Performance of Magnesium Silicate Hydroxide/Ni Composite as an Oil-Based Additive for Steel–Steel Contact

Strengthening mechanism of different morphologies of nano-sized MSH on tribological performance of phosphate/MoS2 bonded solid lubricating coatings

Synergistic dispersion, adsorption, and anti-wear effects of magnesium silicate hydroxide nanomaterials and carboxylic acid

In situ tribological regulation behavior induced by MSH@LaF 3 in phosphate/MoS 2 bonded solid lubricating coatings

Compaction of Hydrophobic Molybdenum Disulfide Coatings for Promoting Tribological Behaviors on Engineering Steel

Tribological Behavior of Fe3o4/Mos2 Nanocomposites Additives in Aqueous and Oil Phase Media

The Synergistic Antiwear and Frictional Properties of Organic Molybdenum Compound with Zinc Dialkyldithiophosphate

The Application of Nano-MoS2 Quantum Dots as Liquid Lubricant Additive for Tribological Behavior Improvement

Tribological mechanisms of the synergistic effect between sulfur- and phosphorus-free organic molybdenum and ZDDP

2D/2D HETEROSTRUCTURE OF FLOWER-LIKE MoS2 NANOSPHERES ANCHORED ON g-C3N4 NANOSHEETS FOR REDUCING FRICTION AND WEAR

Tribological properties of magnetron sputtered MoS2/metal (Ti, Mo) nanocomposite coatings

Tribological Properties of Molybdenum Disulphide Nanoparticles in Soybean Oil